Abstract
Semi-solid AZ91D magnesium alloy billets were prepared by near-liquidus heat holding. Semi-solid squeeze casting was conducted at 575, 585 and 595 °C, respectively, with 1 mm·s−1 squeeze speed. The semisolid squeeze casting AZ91D samples were heat treated by T4 (solution at 415 °C for 24 h) and T6 (solution at 415 °C for 24 h + 220 °C for 8 h) processes, respectively. The microstructure and mechanical properties of the alloy in different states were investigated by means of OM, SEM and tensile testing machine. The results show that compared to as-cast alloy, the grain size of the semi-solid squeezed AZ91D decreased significantly, and with the increase of semi-solid squeeze temperature, the grain size of AZ91D increased. The grains of the alloy were refined by T4 treatment, and further refined by T6 treatment. T6 treatment greatly improved the tensile strength, elongation, and hardness, but did not significantly improve yield strength. After 575 °C squeeze casting and T6 treatment, the ultimate tensile strength (UTS) reached 285 MPa, the elongation reached 13.36%, and the hardness also reached the maximum (106.8 HV), but the yield strength (YS) was only 180 MPa. During the process of semi-solid squeeze casting and heat treatment, the matrix grain was refined and a large number of precipitated and secondary precipitated phases of Mg17Al12 appeared. Both the average size of matrix grain and secondary precipitated phase decreased, while the volume fraction of secondary precipitated phase increased. All these resulted in high tensile strength, elongation and hardness.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Bahrami A, Razaghian A, Emamy M, et al. Microstructure and tensile properties of Al-15wt.%Mg2Si composite after hot extrusion and heat treatment. Key Engineering Materials, 2011, 1213(943): 1171–1176.
Wang Xiaojun, Hu Xiaoshi, Nie Kaibo, et al. Hot extrusion of SiCp/AZ91 Mg matrix composites. Transactions of Nonferrous Metals Society of China, 2012, 22(8): 1912–1917.
Chen Tian, Xie Zhiwen, Luo Zhuangzhu, et al. Microstructure evolution and tensile mechanical properties of thixoformed AZ61 magnesium alloy prepared by squeeze casting. Transactions of Nonferrous Metals Society of China, 2014, 24(11): 3421–3428.
Kleiner S, Beffort O, Wahlen A, et al. Microstructure and mechanical properties of squeeze cast and semi-solid cast Mg-Al alloys. Journal of Light Metals, 2002, 2(4): 277–280.
Tang Zhongxue, Li Yuandong, Hao Yuan. Effects of aging treatment on microstructures and mechanical properties of thixoformed AZ91D magnesium alloy. Hot Working Technology, 2005, 3: 4–7. (In Chinese)
Li Yuandong, Tang Zhongxue, Hao Yuan, et al. Investigation of solid-solution and aging treatment of thixoformed alloy AZ91D. Journal of Lanzhou University of Technology, 2005, 31(5): 15–18. (In Chinese)
Sun Xuefei, Wang Cuiju, Deng Kunkun, et al. Aging behavior of AZ91 matrix influenced by 5 µm SiCp: Investigation on the microstructure and mechanical properties. Journal of Alloys and Compounds, 2017, 727: 1263–1272.
Qi Yesi, Chen Tijun, Li Yuanning, et al. Effects of solution treatment time on microstructure and mechanical properties of thixoformed AZ63 magnesium alloy. Special Casting & Nonferrous Alloys, 2013, 33(12): 1127–1131. (In Chinese)
Dong Qing, Luo Zhe, Zhu Hong, et al. Basal-plane stacking-fault energies of Mg alloys: A first-principles study of metallic alloying effects. Journal of Materials Science and Technology, 2018, 34(10): 1773–1780.
Zhang Li, Deng Kunkun. Microstructures and mechanical properties of SiCp/Mg-xAl-2Ca composites collectively influenced by SiCp and Al content. Materials Science and Engineering: A, 2018, 725: 510–521.
Peng Guosheng, Chen Kanghua, Chen Songyi, et al. Evolution of the second phase particles during the heating-up process of solution treatment of Al-Zn-Mg-Cu alloy. Materials Science & Engineering A, 2015, 641: 237–241.
Sun Xuefei, Wang Cuiju, Deng Kunkun, et al. High strength SiCp/AZ91 composite assisted by dynamic precipitated Mg17Al12 phase. Journal of Alloys and Compounds, 2018, 732: 328–335.
Wang Huiyuan, Zhang Enbo, Nan Xiaolong, et al. A comparison of microstructure and mechanical properties of Mg-9Al-1Zn sheets rolled from as-cast, cast-rolling and as-extruded alloys. Materials & Design, 2016, 89: 167–172.
Wang Xiaojun, Wu Kun, Huang Wenxian, et al. Study on fracture behavior of particulate reinforced magnesium matrix composite using in situ SEM. Composites Science and Technology, 2007, 67(11–12): 2253–2260.
Zhao Pin, Shen Huanxiang, Zhao Ensheng. Decomposition products and properties of supercooled β phase of Zn-27A1-2.7Cu-0.03Mg-0.5Mn alloy. Non-ferrous Metal, 2004, 56(2): 1–7. (In Chinese)
Author information
Authors and Affiliations
Corresponding author
Additional information
Zhi-yong You
Male, born in 1971. Associate Professor. Research interests: magnesium and aluminum matrix composites, research and application of laser rapid manufacturing technology.
Rights and permissions
About this article
Cite this article
You, Zy., Jiang, Ax., Duan, Zz. et al. Effect of heat treatment on microstructure and properties of semi-solid squeeze casting AZ91D. China Foundry 17, 219–226 (2020). https://doi.org/10.1007/s41230-020-9103-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-020-9103-9