Influence of Oxyfluorination on Geometrical Pull-Out Behavior of Carbon-Fiber-Reinforced Epoxy Matrix Composites

  • Article
  • Published:
Macromolecular Research Aims and scope Submit manuscript

Abstract

To improve the interfacial adhesion between carbon fibers and an epoxy matrix, carbon fibers were modified by oxyfluorination at different temperature conditions. Surface analyses of the oxyfluorinated carbon fibers were performed using scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and dynamic contact angle measurements. The interfacial shear strength (IFSS) of a single carbon fiber/epoxy matrix was studied by employing single-fiber pull-out tests to confirm the interfacial adhesion. The pull-out behavior of the fiber from the matrix was discussed based on the Greszczuk’s geometrical model. Functional groups such as C-F, C-O, and COOH were present on the carbon fiber surfaces after oxyfluorination. Moreover, the presence of functional groups increased the surface polarity of the fibers, resulting in an increase in the IFSS owing to the improvement of the interfacial adhesive strength between the carbon fibers and the epoxy matrix.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. S. J. Park, Carbon Fibers, Springer, Dordrecht, 2015.

    Google Scholar 

  2. K. Naito, Y. Tanaka, and J. M. Yang, Carbon, 118, 168 (2017).

    Article  CAS  Google Scholar 

  3. Z. S. Wu, Y. Zheng, S. Zhen, S. Wang, C. Sun, K. Parvez, T. Ikeda, X. Bao, K. Mullen, and X. Feng, Adv. Mater., 29, 1602960 (2017).

    Article  CAS  Google Scholar 

  4. B. Mensah, S. I. Kang, W. Wang, and C. Nah, Mech. Adv. Mater. Mod. Process., 4, 1 (2018).

    Article  Google Scholar 

  5. S. Yu, K. Park, J. W. Lee, S. M. Hong, C. Park, T. H. Han, and C. M. Koo, Macromol. Res., 25, 559 (2017).

    Article  CAS  Google Scholar 

  6. A. Borenstein, O. Hanna, R. Attias, S. luski, T. Brousse, and D. Aurbach, J. Mater. Chem. A, 5, 12653 (2017).

    Article  CAS  Google Scholar 

  7. Y. J. Yim and S. J Park, Bull. Korean Chem. Soc., 38, 191 (2017).

    Article  CAS  Google Scholar 

  8. Y. J. Yim and S. J Park, J. Ind. Eng. Chem., 21, 155 (2015).

    Article  CAS  Google Scholar 

  9. D. D. L. Chung, Carbon Fiber Composites, Elsevier, Boston, 1994.

    Google Scholar 

  10. J. Ren, W. Bai, G. Guan, Y. Zhang, and H. Peng, Adv. Mater., 25, 5965 (2013).

    Article  CAS  PubMed  Google Scholar 

  11. J. Zhu, S. W. Park, H. I. Joh, H. C. Kim, and S. Lee, Macromol. Res., 23, 79 (2015).

    Article  CAS  Google Scholar 

  12. Y. J. Yim, K. Y. Rhee, and S. J. Park, Compos. Part B, 76, 286 (2015).

    Article  CAS  Google Scholar 

  13. B. Jiang, T. Zhang, L. Zhao, and Y. Huang, Compos. Sci. Technol., 140, 39 (2017).

    Article  CAS  Google Scholar 

  14. S. J. Park and Y. M. Kim, Mater. Sci. Eng. A, 391, 121 (2005).

    Article  CAS  Google Scholar 

  15. S. H Lee, J. Y. Kim, C. M. Koo, and W. N. Kim, Macromol. Res., 25, 936 (2017).

    Article  CAS  Google Scholar 

  16. Y. J. Yim and S. J. Park, Compos. Res., 28, 361 (2015).

    Article  Google Scholar 

  17. S. M. Cho and H. T. Jung, Macromol. Res., 22, 1066 (2014).

    Article  CAS  Google Scholar 

  18. Y. K. Lee, S. H. Jang, M. S. Kim, W. N. Kim, H. G. Yoon, S. D. Park, S. T. Kim, and J. D. Lee, Macromol. Res., 18, 241 (2010).

    Article  CAS  Google Scholar 

  19. S. J. Park and J. R. Lee, J. Mater. Sci., 33, 647 (1998).

    Article  CAS  Google Scholar 

  20. Y. J. Yim and S. J. Park, Carbon Lett., 22, 36 (2017).

    Google Scholar 

  21. J. H. Lee, K. Y. Rhee, and S. J. Park, Compos. Part A, 42, 478 (2011).

    Article  CAS  Google Scholar 

  22. S. J. Park and B. J. Park, J. Mater. Sci. Lett., 18, 47 (1999).

    Article  CAS  Google Scholar 

  23. F. L. Jin and S. J. Park, Carbon Lett., 16, 67 (2015).

    Article  Google Scholar 

  24. M. T. Kim, K. Y. Rhee, J. H. Lee, D. Hui, and A. Lau, Compos. Part B, 42, 1257 (2011).

    Article  CAS  Google Scholar 

  25. N. Li, Y. Li, J. Jelonnek, G. Link, and J. Gao, Compos. Part B, 122, 61 (2017).

    Article  CAS  Google Scholar 

  26. Y. J. Yim and S. J. Park, Compos. Part B, 131, 144 (2017).

    Article  CAS  Google Scholar 

  27. S. J. Park and M. K. Seo, Interface Science and Composites, Elsevier, (2011).

    Google Scholar 

  28. E. P. Plueddemann, Interfaces in Polymer Matrix Composites: Composite Materials, Elsevier (2016).

    Google Scholar 

  29. M. Sharma, S. Gao, E. Mader, H. Sharma, L. Y. Wei, and J. Bijwe, Compos. Sci. Technol., 102, 35 (2014).

    Article  CAS  Google Scholar 

  30. X. Yuan, B. Zhu, X. Cai, J. Liu, K. Qiao, and J. Yu, Appl. Surf. Sci., 401, 414 (2017).

    Article  CAS  Google Scholar 

  31. M. Andideh and M. Esfandeh, Compos. Sci. Technol., 134, 132 (2016).

    Article  CAS  Google Scholar 

  32. S. J. Park, Y. S. Jang, and K. Y. Rhee, J. Colloid Interface Sci., 245, 383 (2002).

    Article  CAS  PubMed  Google Scholar 

  33. M. H. Kim, K. Y. Rhee, H. J. Kim, and D. H. Jung, Mater. Sci. Eng. A, 448, 1 (2007).

    Article  CAS  Google Scholar 

  34. Z. Jin, Z. Zhang, and L. Meng, Mater. Chem. Phys., 97, 167 (2006).

    Article  CAS  Google Scholar 

  35. S. J. Park, M. K. Seo, and Y. S. Lee, Carbon, 41, 723 (2003).

    Article  CAS  Google Scholar 

  36. Y. J. Yim, K. Y. Rhee, and S. J. Park, Compos. Part B, 98, 120 (2016).

  37. L. Rooyen, H. Bissett, M. C. Khoathane, and J. Karger-kocsis, Carbon, 109, 30 (2016).

    Article  CAS  Google Scholar 

  38. S. J. Park, H. J. Jeong, and C. W. Nah, Mater. Sci. Eng. A, 385, 13 (2004).

    Article  CAS  Google Scholar 

  39. S. J. Park, M. K. Seo, and K. Y. Rhee, Mater. Sci. Eng. A, 356, 219 (2003).

    Article  CAS  Google Scholar 

  40. I. Kruppke, M. Bartusch, R. Hickmann, R. D. Hund, and C. Cherif, Molecules, 21, 1127 (2016).

    Article  Google Scholar 

  41. S. J. Park, Interfacial Forces and Field: Theory and Applications, J. P. Hsu, Ed., Marcel Dekker, New York, 1999.

  42. S. J. Park, M. S. Cho, and J. R. Lee, J. Colloid Interface Sci., 226, 60 (2000).

    Article  CAS  PubMed  Google Scholar 

  43. S. Meretz, W. Auersch, C. Marotzke, E. Schulz, and A. Hampe, Compos. Sci. Technol., 48, 285 (1993).

    Article  CAS  Google Scholar 

  44. Y. C. Kim and S. J. Park, J. Appl. Polym. Sci., 74, 15 (1999).

    Article  CAS  Google Scholar 

  45. G. Desarmot and J. P. Favre, Compos. Sci. Technol., 42, 151 (1991).

    Article  CAS  Google Scholar 

  46. L. B. Greszczuk, ASTM STP, 452, 42 (1969).

    Google Scholar 

  47. J. S. Im, S. C., Kang, B. C. Bai, T. S. Bae, S. J. In, E. Jeong, S. H. Lee, and Y. S. Lee, Carbon, 49, 2235 (2011).

    Article  CAS  Google Scholar 

  48. Y. Hattori, N. Noguchi, F. Okino, H. Touhara, Y. Nakahigashi, S. Utsumi, H. Tanaka, H. Kanoh, and K. Kaneko, Carbon, 45, 1391 (2007).

    Article  CAS  Google Scholar 

  49. P. E. Pehrsson, W. Zhao, J. W. Baldwin, C. Song, J. Liu, S. Kooi, and B. Zheng, J. Phys. Chem. B, 107, 5690 (2003).

    Article  CAS  Google Scholar 

  50. N. Bartlett, T. Mallouk, F. Okino, G. Rosenthal, and J. Verniolle, J. Fluor. Chem., 23, 409 (1983).

    Article  Google Scholar 

  51. A. Bismark, R. Tahhan, J. Spriner, A. Schulz, T. M. Klapötke, H. Zell, and W. Michaeli, J. Fluor. Chem., 84, 127 (1997).

    Article  Google Scholar 

  52. S. J. Park and M. S. Cho, Carbon, 38, 1053 (2000).

    Article  CAS  Google Scholar 

  53. S. J. Park, W. B. Park, and J. R. Lee, J. Mater. Sci., 35, 6151 (2000).

    Article  CAS  Google Scholar 

  54. H. I. Kim, W. K. Choi, S. Y. Oh, M. K. Seo, S. J. Park, K. H. An, Y. S. Lee, and B. J. Kim, J. Nanosci. Nanotechnol., 14, 9097 (2014).

    Article  CAS  PubMed  Google Scholar 

  55. M. K. Seo and S. J. Park, Macromol. Res., 17, 430 (2009).

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Chemistry, Inha University, 100 Inharo, Nam-gu, Incheon, 22212, Korea

    Yoon-Ji Yim & Soo-Jin Park

  2. Ocean ICT & Advanced Materials Technology Research Division, Research Institute of Medium & Small Shipbuilding, 38-6, Noksansandan 232, Kangseo-gu, Busan, 46757, Korea

    Kyong-Min Bae

Authors
  1. Yoon-Ji Yim
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Kyong-Min Bae
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Soo-Jin Park
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Soo-Jin Park.

Additional information

Acknowledgments: This research was supported by The Leading Human Resource Training Program of Regional Neo industry through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT and future Planning (grant number) (NRF-2016H1D5A1909732) and the Technological Innovation R&D Program (S2475164) funded by the Small and Medium Business Administration (SMBA, Korea).

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Yim, YJ., Bae, KM. & Park, SJ. Influence of Oxyfluorination on Geometrical Pull-Out Behavior of Carbon-Fiber-Reinforced Epoxy Matrix Composites. Macromol. Res. 26, 794–799 (2018). https://doi.org/10.1007/s13233-018-6115-z

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13233-018-6115-z

Keywords

Search

Navigation