Local laser heat treatment of ultra high strength steels to improve formability

  • Production Process
  • Published:
Production Engineering Aims and scope Submit manuscript

Abstract

Ultra high strength steels are of enormous interest especially in the automotive industry due to their potential in realising light weight structures and improving the crash behaviour. However the poor formability of these steels limits their application for many parts in the car body. A solution to this limitation can be a local heat treatment using a laser beam to soften the material where a high formability is needed. Laser treatment was performed using a Nd:YAG laser with 3 kW maximum power. The output power was temperature controlled to achieve a constant temperature level during the heat treatment. Large areas are treated by scanning the surface with the laser beam. The materials under investigation are dual phase (DP), retained austenite (RA) and martensitic (MS) steels with a tensile strength of 600–1,200 MPa. The microstructure of DP steels consists of martensite and ferrite. RA steels contain ferrite, martensite and additionally a certain amount of retained austenite which transforms into martensite during plastic flow. MS steels are fully martensitic which gives them the highest yield strength of all UHS steels. The various steels were provided as not galvanised sheets (hot or cold rolled) with a thickness of 1.5 mm. Depending on material and process parameters tempering of martensite, formation of ferrite and transformation of retained austenite to martensite are observed as a result of the heat treatment. Tensile tests of DP 600, DP 1000 and MS-W 1200 reveal a significant reduction in yield and tensile strength and an increase in elongation after LHT. The effect is due to tempering of martensite and in the case of MS-W also due to an increase in volume fraction of ferrite. Tensile tests of RA-K 700 reveal a minor reduction in yield and tensile strength and a decrease in elongation. This can be attributed to the lower content of retained austenite which has transformed into martensite during LHT. From this result it can be expected that LHT is not beneficial for high deformation degrees. Deep drawing of a mock-up geometry using MS-W 1200 and RA-K 700 showed a significant decrease in slide force (~20%) compared to the initial condition. This results show that laser heat treatment has the potential to improve formability of UHS steels.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. n.n., (2002) Bessere Teilequalität beim Tiefziehen von Bauteilen aus hochfesten Stählen, Bleche, Rohre, Profile, Band 49(4): 36–39

  2. Yamazaki K (2003) Current situation and properties of ultra-high strength steel for automotive use in Japan. Rev Met Paris 7–8:779–786

    Article  Google Scholar 

  3. n.n., (1996) Sonderausgabe Werkstoffe im Automobilbau, Motortechnische Zeitschrift, Band 57:52–54

  4. Kerausch M, Giera A, Geiger M (2003) Improved deep drawabilityof aluminium blanks by local laser heat treatment. In: Geiger M, Otto A (eds), Proceeding of 4th International Conference LANE, 2004, Erlangen, Germany, 21–24 Sept 2003, pp 1135–1146

  5. Kerausch M, Giera A, Geiger M (2003) Improved material flow for deep drawing of aluminium blanks by local laser heat treatment. In: Kals HJJ, Shirvani B, Sing UP, Geiger M (eds), Proceedings of 10th International Conference on Sheet Metal, SheMet 2003, University of Ulster, Jordantown (Ireland), 14–16 April 2003, pp 73–80

  6. Bergmann W (1997) Karosserieleichtbau mit höherfesten Stählen: Gewichtsreduzierung durch Umformen von höherfesten Stahlblechen mit partiell veränderten Kennwerten, Presentation at Leichtbau ‘97

  7. Zajac J, Formability of Laser Annealed UHSS DP steels, SIMR-report, IM-2001-016

  8. Weisheit A, Vitr G, Wissenbach K, Zajac J, Thoors H, Johansson B, Ribera E, Arino J, Sierra F (2005) Local heat treatment of ultra high strength steels to improve formability. In Vollertsen F, Seefeld T (eds), 1th International Workshop on Thermal Forming, IWOTE 05, Bremen, Germany, 14–16 April 2005, pp 63–81

  9. Neugebauer R, Scheffler S, Poprawe R, Vitr G (2006) Verbesserung der Umformeigenschaften von schwer umformbaren Werkstoffen durch lokal vorinitialisierten Wärmeeintrag, EFB-Forschungsbericht Nr. 251, 2006

Download references

Author information

Authors and Affiliations

  1. Fraunhofer Institute for Machine Tools and Forming Technology IWU, Chemnitz, Germany

    Reimund Neugebauer & Sören Scheffler

  2. Fraunhofer Institute for Laser Technology, Aachen, Germany

    Reinhart Poprawe & Andreas Weisheit

Authors
  1. Reimund Neugebauer
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Sören Scheffler
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Reinhart Poprawe
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Andreas Weisheit
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Reimund Neugebauer.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Neugebauer, R., Scheffler, S., Poprawe, R. et al. Local laser heat treatment of ultra high strength steels to improve formability. Prod. Eng. Res. Devel. 3, 347 (2009). https://doi.org/10.1007/s11740-009-0186-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11740-009-0186-9

Keywords

Search

Navigation