Abstract
Various types of shot peening treatments were applied to duplex stainless steel. The effects of shot peening intensity and working procedures on the microstructure were investigated. The domain size and microstrain evolution in the surface layer were characterized utilizing the Rietveld method. As the shot peening intensity increased, the surface roughness increased in the surface layer; however, it decreased after multiple (dual and triple) shot peening. The mole fraction of strain-induced martensite as a function of the intensity of shot peening was evaluated by XRD measurements. Both potentiodynamic polarization curves and salt spray tests of shot-peened samples in NaCl solution were investigated. The results indicate that traditional shot peening has negative effects on corrosion resistance with increasing shot peening intensity; however, the corrosion rate can be reduced by means of multiple shot peening.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
D.H. Mesa, C.E. Pinedo, and A.P. Tschiptschin, Improvement of the Cavitation Erosion Resistance of UNS S31803 Stainless Steel by Duplex Treatment, Surf. Coat. Technol., 2010, 205, p 1552–1556
A.I. Munoz, J.G. Anton, J.L. Guinon, and V.P. Herranz, Inhibition Effect of Chromate on the Passivation and Pitting Corrosion of a Duplex Stainless Steel in LiBr Solutions Using Electrochemical Techniques, Corros. Sci., 2007, 49, p 3200–3225
Z. Wei, J. Laizhu, H. Jincheng, and S. Hongme, Study of Mechanical and Corrosion Properties of a Fe-21.4Cr-6Mn-1.5Ni-0.24N-0.6Mo Duplex Stainless Steel, Sci. Eng. A, 2008, 497, p 501–504
E.A.M. Hussain and M.J. Robinson, Erosion-Corrosion of 2205 Duplex Stainless Steel in Flowing Seawater Containing Sand Particles, Corros. Sci., 2007, 49, p 1737–1754
Q. Feng, C. Jiang, Z. Xu, L. Xie, V. Ji, and K. Zhan, Effect of Shot Peening on the Residual Stress and Microstructure of Duplex Stainless Steel, Surf. Coat. Technol., 2013, 226, p 140–144
K. Zhan, C. Jiang, X. Wu, and V. Ji, Surface Layer Characteristics of S30432 Austenite Stainless Steel After Shot Peening, Mater. Trans., 2012, 53, p 1002–1006
G.D. Byrne, L. O’Neill, B. Twomey, and D.P. Dowling, Comparison Between Shot Peening and Abrasive Blasting Processes as Deposition Methods for Hydroxyapatite Coatings onto a Titanium Alloy, Surf. Coat. Technol., 2013, 216, p 224–231
B.E. Warren, X-ray Diffraction, Addison-Wesley, MA, 1969, p 169–172
L. Lutterotti, Maud Version 2.33, 2011, (http://www.ing.unitn.it/maud/).
ASTM G31-72, Standard Practices for Laboratory Immersion Corrosion Testing of Metals, vol. 03.02, 2004.
V. Shrinivas, S.K. Varma, and L.E. Murr, Deformation-Induced Martensitic Characteristics in 304 and 316 Stainless Steels During Room-Temperature Rolling Metall, Trans. A, 1995, 26, p 661–671
I. Altenberger, B. Scholtes, U. Martin, and H. Oettel, Cyclic Deformation and Near Surface Microstructures of Shot Peened or Deep Rolled Austenitic Stainless Steel AISI, 304, Sci. Eng. A, 1999, 264, p 1–16
H. Kaesche, Die Korrosion der Metalle, Springer, Berlin, 1979
X.Y. Wang, M.S. Wu, L. Zhang et al., Corrosion Behavior in 3.5% NaCl Solution of 316 SS Passinated in an Oxidizing Acid Liquor, Corros. Sci. Technol. Prot. , 2000, 12, p 311–314
D.Y. Hwang, B.Y. Yoo, J.Y. Cho, D.H. Lee, and D.H. Shin, Corrosion Resistance of Oxide Layers Formed on AZ91 Mg Alloy in KMnO4 Electrolyte by Plasma Electrolytic Oxidation, Electrochim. Acta., 2009, 54, p 5479–5485
E. Arslan, Y. Totik, E. Demirci, and A. Alsaran, Influence of Surface Roughness on Corrosion and Tribological Behavior of CP-Ti After Thermal Oxidation Treatment, J. Mater. Eng. Perform, 2010, 19, p 428–433
A. Barbucci, M. Delucchi, M. Panizza, M. Sacco, and G. Cerisola, Electrochemical and Corrosion Behaviour of Cold Rolled AISI, 301 in 1 M H2SO4, J. Alloys Compd., 2001, 317–318, p 607–611
B. Mazza, P. Pedeferri, D. Sinigaglia, A. Cigada, G. Fumagalli, and G. Re, Electrochemical and Corrosion Behaviour of Work-Hardened Commercial Austenitic Stainless Steels in Acid Solutions, Corros. Sci., 1979, 19, p 907–921
S.V. Phadnis, A.K. Satpati, K.P. Muthe, J.C. Vyas, and R.I. Sundaresan, Comparison of Rolled and Heat Treated SS304 in Chloride Solution Using Electrochemical and XPS Techniques, Corros. Sci., 2003, 45, p 2467–2483
Y. Li, F. Wang, and G. Liu, Grain Size Effect on the Electrochemical Corrosion Behavior of Surface Nanocrystallized Low-Carbon Steel, Corrosion, 2004, 60, p 891–896
Y.W. Hao, B. Deng, C. Zhong, Y.M. Jiang, and J. Li, Effect of Surface Mechanical Attrition Treatment on Corrosion Behavior of 316 Stainless Steel, J. Iron Steel Res. Int., 2009, 16, p 68–72
A. Di Schino and J.M. Kenny, Effects of the Grain Size on the Corrosion Behavior of Refined AISI, 304 Austenitic Stainless Steels, Mater. Sci. Lett., 2002, 21, p 1631–1634
D. Song, A. Ma, J. Jiang, P. Lin, D. Yang, and J. Fan, Corrosion Behavior of Equal-Channel-Angular-Pressed Pure magnesium in NaCl Aqueous Solution, Corros. Sci., 2010, 52, p 481–490
W. Li and D.Y. Li, Variations of Work Function and Corrosion Behaviors of Deformed Copper Surfaces, Appl. Surf. Sci., 2005, 240, p 388–395
J.Z. Lu, K.Y. Luo, D.K. Yang, X.N. Cheng, J.L. Hu, F.Z. Dai, H. Qi, L. Zhang, J.S. Zhong, Q.W. Wang, and Y.K. Zhang, Effects of Laser Peening on Stress Corrosion Cracking (SCC) of ANSI, 304 Austenitic Stainless Steel, Corros. Sci., 2012, 60, p 145–152
Acknowledgment
This research work is supported by the Chengdu Normal University Talent introduction scientific research special project (YJRC2015-3).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Feng, Q., She, J., Wu, X. et al. The Effect of Multiple Shot Peening on the Corrosion Behavior of Duplex Stainless Steel . J. of Materi Eng and Perform 27, 1396–1403 (2018). https://doi.org/10.1007/s11665-018-3204-2
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-018-3204-2