The effect of Mg on the microstructure and mechanical behavior of Al-Si-Mg casting alloys

  • Published:
Metallurgical and Materials Transactions A Aims and scope Submit manuscript

Abstract

The microstructure and tensile behavior of two Al-7 pct Si-Mg casting alloys, with magnesium contents of 0.4 and 0.7 pct, have been studied. Different microstructures were produced by varying the solidification rate and by modification with strontium. An extraction technique was used to determine the maximum size of the eutectic silicon flakes and particles. The eutectic Si particles in the unmodified alloys and, to a lesser extent, in the Sr-modified alloys are larger in the alloys with higher Mg content. Large Fe-rich π-phase (Al9FeMg3Si5) particles are formed in the 0.7 pct Mg alloys together with some smaller β-phase (Al5FeSi) plates; in contrast, only β-phase plates are observed in the 0.4 pct Mg alloys. The yield stress increases with the Mg content, although, at 0.7 pct Mg, it is less than expected, possibly because some of the Mg is lost to π-phase intermetallics. The tensile ductility is less in the higher Mg alloys, especially in the Sr-modified alloys, compared with the lower Mg alloys. The loss of ductility of the unmodified alloy seems to be caused by the larger Si particles, while the presence of large π-phase intermetallic particles accounts for the loss in ductility of the Sr-modified alloy.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. G.A. Edwards, K. Stiller, G.L. Dunlop, and M.J. Couper: Mater. Sci. Forum, 1996, vols. 217–222, pp. 713–8.

    Google Scholar 

  2. H.W. Zandbergen, S.J. Andersen, and J. Jansen: Science, 1997, vol. 277, pp. 1221–5.

    Article  CAS  Google Scholar 

  3. R.C. Harris, S. Lipson, and H. Rosenthal: AFS Trans., 1956, vol. 64, pp. 470–81.

    Google Scholar 

  4. S.F. Frederick and W.A. Bailey: Trans. TMS-AIME, 1968, vol. 242, pp. 2063–7.

    CAS  Google Scholar 

  5. R. Sinfield and D.A. Harris: J. Aus. Inst. Met., 1975, vol. 20, pp. 44–8.

    Google Scholar 

  6. J.A. Eady and D.M. Smith: Mater. Forum, 1986, vol. 9, pp. 217–23.

    CAS  Google Scholar 

  7. S. Shivkumar, C. Keller, and D. Apelian: AFS Trans., 1990, vol. 98, pp. 905–10.

    CAS  Google Scholar 

  8. K.T. Kashyap, S. Murali, K.S. Raman, and K.S.S. Murthy: Mater. Sci. Technol., 1993, vol. 9, pp. 189–203.

    CAS  Google Scholar 

  9. S. Murali, K.S. Raman, and K.S.S. Murthy: Mater. Sci. Eng., 1992, vol. A151, pp. 1–10.

    CAS  Google Scholar 

  10. A.T. Joenoes and J.E. Gruzleski: Cast Met., 1991, vol. 4, pp. 62–71.

    Google Scholar 

  11. B. Closset and J.E. Gruzleski: Metall. Trans. A, 1982, vol. 13A, pp. 945–51.

    CAS  Google Scholar 

  12. G. Gustafsson, T. Thorvaldsson, and G.L. Dunlop: Metall. Trans. A, 1986, vol. 17A, pp. 45–52.

    CAS  Google Scholar 

  13. G.E. Nagel, J.P. Mouret, and J. Dubruelh: AFS Trans., 1983, vol. 91, pp. 157–60.

    CAS  Google Scholar 

  14. D.A. Granger, R.R. Sawtell, and M.M. Kersker: AFS Trans., 1984, vol. 92, pp. 579–86.

    CAS  Google Scholar 

  15. G.K. Sigworth, S. Shivkumar, and D. Apelian: AFS Trans., 1989, vol. 97, pp. 811–24.

    Google Scholar 

  16. Y.H. Tan, S.L. Lee, and Y.L. Lin: Metall. Mater. Trans. A, 1995, vol. 26A, pp. 1195–205.

    CAS  Google Scholar 

  17. C. Verdu, H. Cercueil, S. Communal, P. Sainfort, and R. Fougeres: Mater. Sci. Forum, 1996, vols. 217–222, pp. 1449–54.

    Google Scholar 

  18. Q.G. Wang, C.H. Caceres, and J.R. Griffiths: AFS Trans., 1998, vol. 106, pp. 131–6.

    CAS  Google Scholar 

  19. Q.G. Wang and C.H. Caceres: Mater. Sci. Eng., 1997, vols. A234–A236, pp. 106–9.

    Google Scholar 

  20. Q.G. Wang and C.H. Caceres: Mater. Sci. Forum, 1996, vol. 242, pp. 159–64.

    Article  Google Scholar 

  21. C.H. Caceres and B.I. Selling: Mater. Sci. Eng., 1996, vol. A220, pp. 109–16.

    CAS  Google Scholar 

  22. R.E. Spear and G.R. Gardner: AFS Trans., 1963, vol. 71, pp. 209–15.

    Google Scholar 

  23. D.L. McLellan: AFS Trans., 1982, vol. 90, pp. 173–91.

    CAS  Google Scholar 

  24. C.H. Caceres, C.J. Davidson, and J.R. Griffiths: Mater. Sci. Eng., 1995, vol. A197, pp. 171–9.

    CAS  Google Scholar 

  25. C.H. Caceres and Q.G. Wang: Int. J. Cast Met. Res., 1996, vol. 9, pp. 157–62.

    CAS  Google Scholar 

  26. J.C. Jaquet: 2nd Int. Conf. on Molten Aluminium Processing, AFS, Des Plaines, IL, 1989, pp. 2.1–2.36

    Google Scholar 

  27. C.H. Caceres and Q.G. Wang: AFS Trans., 1996, vol. 104, pp. 1039–43.

    CAS  Google Scholar 

  28. M.S. Misra and K.J. Oswalt: AFS Trans., 1982, vol. 90, pp. 1–10.

    CAS  Google Scholar 

  29. S. Shivkumar, S. Ricci, Jr., B. Steenhoff, D. Apelian, and G.K. Sigworth: AFS Trans., 1989, vol. 97, pp. 791–810.

    Google Scholar 

  30. D.S. Saunders, B.A. Parker, and J.R. Griffiths: J. Aus. Inst. Met., 1975, vol. 20, pp. 33–8.

    CAS  Google Scholar 

  31. R.W. Coade, S.M. Nugent, D.S. Saunders, J.R. Griffiths, and B.A. Parker: Proc. Annual Conf. of the Australasian Institute of Metals, Australasian Institute of Metals, Melbourne, 1977, pp. 6B-1–6B-2.

  32. Q.G. Wang, C.H. Caceres, and J.R. Griffiths: Proc. 9th Int. Conf. on Fracture (ICF9), B.L. Karihaloo, Y.W. Mai, M.I. Ripley, and R.O. Ritchie, eds., Elsevier, London, 1997, pp. 2511–8.

    Google Scholar 

  33. Q.G. Wang and C.H. Caceres: Mater. Sci. Eng., 1998, vol. A241, pp. 72–82.

    CAS  Google Scholar 

  34. C.H. Caceres and J.R. Griffiths: Acta Mater., 1996, vol. 44, pp. 25–33.

    Article  CAS  Google Scholar 

  35. K.J. Oswalt and M.S. Misra: AFS Trans., 1980, vol. 88, pp. 845–62.

    CAS  Google Scholar 

  36. R.S. Chappell, T.A. Hughes, and G. Pollard: Metallography, 1970, vol. 3, pp. 235–7.

    Article  Google Scholar 

  37. E.E. Underwood: Quantitative Stereology, Addison-Wesley, Reading, MA, 1970.

    Google Scholar 

  38. C.J. Simensen and T.L. Rolfsen: Z. Metallkd., 1997, vol. 88, pp. 142–6.

    CAS  Google Scholar 

  39. J.M. Dowling and J.W. Martin: Acta Metall., 1976, vol. 24, pp. 1147–53.

    Article  CAS  Google Scholar 

  40. A. Kelly: Phil. Mag., 1958, vol. 3, pp. 1472–4.

    Google Scholar 

  41. C.H. Caceres, C.J. Davidson, J.R. Griffiths, L.M. Hogan, and Q.G. Wang: Mater. Forum, 1997, vol. 21, pp. 27–43.

    CAS  Google Scholar 

  42. Aerospace Structural Metals Handbook, W. F. Brown, H. Mindlin, and C.Y. Ho, eds., CINDAS/USAF CRDA Handbooks Operation, Purdue University, West Lafayette, IN, 1959 (1995 revision, Figure 1.0918).

    Google Scholar 

  43. C.H. Caceres, J.R. Griffiths, and P. Reiner: Acta Mater., 1996, vol. 44, pp. 15–23.

    Article  CAS  Google Scholar 

Download references

Author information

Author notes

  1. Q. G. Wang (Research Student, Research Associate)

    Present address: the CRC for Alloy and Solidification Technology (CAST), Department of Mining, Minerals and Materials Engineering, The University of Queensland, 4072, Brisbane, Australia

Authors and Affiliations

  1. the CRC for Alloy and Solidification Technology (CAST), Department of Mining, Minerals and Materials Engineering, The University of Queensland, 4072, Brisbane, Australia

    C. H. Caceres (Senior Lecturer)

  2. CSIRO Manufacturing Science and Technology, 4069, Kenmore, Australia

    C. J. Davidson (Principal Research Scientist) & J. R. Griffiths (Senior Principal Research Scientist)

  3. Metal Processing Institute, SPI, 01609, Worcester, MA

    Q. G. Wang (Research Student, Research Associate)

Authors
  1. C. H. Caceres
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. C. J. Davidson
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. J. R. Griffiths
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Q. G. Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Caceres, C.H., Davidson, C.J., Griffiths, J.R. et al. The effect of Mg on the microstructure and mechanical behavior of Al-Si-Mg casting alloys. Metall Mater Trans A 30, 2611–2618 (1999). https://doi.org/10.1007/s11661-999-0301-8

Download citation

  • Received:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11661-999-0301-8

Keywords

Search

Navigation