Abstract
NiTi wires were brazed together via liquid eutectic formation between NiTi and Nb powders deposited at the wire contact region. The brazed region shows proeutectic NiTi(Nb) in contact with the wires, sandwiching a NiTi-Nb eutectic structure, whose microhardness and stiffness, as characterized via nanoindentation, are higher than the NiTi wires, while also showing signs of high ductility. NiTi-Nb eutectic bonding may thus be a viable approach for producing shape-memory NiTi scaffolds brazed from stacked, woven, or braided wires.
References
L.G. Machado, M.A. Savi: Braz. J. Med. Biol. Res, 2003, vol. 36, no.(6), pp. 683–91.
A. Biesiekierski, J. Wang, M.A.H. Gepreel, C. Wen : Acta Biomater, 2012, vol. 8, no.(5), pp.1661-1669.
Y.P. Zhang, D.S. Li, X.P. Zhang: Scr. Mater, 2007, vol. 57, no.(11), pp. 1020–23.
A. Bansiddhi, T.D. Sargeant, S.I. Stupp, D.C. Dunand : Acta Biomater, 2008, vol.4, no.(4), pp. 773-782.
X.M. Liu, S.L. Wu, K.W.K. Yeung, Y.L. Chan, T. Hu, Z.S. Xu, X.Y. Liu, J.C.Y. Chung, K.M.C. Cheung, P.K. Chu : Biomater, 2011, vol.32, no.(2), pp.330-338.
D.S. Gr ummon, J.A. Shaw, J. Foltz: Mater. Sci. Eng. A, 2006, vol. 438-440, pp.1113-1118.
D.S. Grummon, J.A. Shaw, A. Gremillet: J. Appl. Phys. Lett, 2003, 82:16, pp. 2727–29.
P.A. Michailidis, N. Triantafyllidis, J.A. Shawa, D.S.Grummon: Int. J. Solids Struct., 2009, vol.46, no.(13), pp. 2724–38.
H.N.G. Wadley, N.A. Fleck, A.G. Evans: Compos.Sci.Technol, 2003, vol.63, no.(16), pp.2331-2343.
J.S. Park, J.H. Joo, B.C. Lee, K.J. Kang: Int. J. Mech. Sci, 2011, vol. 53, no.(1), pp. 65–73.
K.J. Kang: Acta Mater, 2009, vol.57, no.(6), pp.1865-1874.
M.G. Lee, G.D. Ko, J. Song, K.J. Kang: Mater. Sci. Eng. A, 2012, vol.539, pp.185-193.
R.W. Fonda, M.J. Scherr, A.B. Geltmacher, K.W. Sharp: J. Mater. Eng. Perform, 2013, vol.22, no. (11), pp.3376-3380.
W. Cai, X.L. Lu, L.C. Zhao : Mater. Sci. Eng. A, 2005, vol.394, no.(1-2), pp.78-82.
H. Shi, S. Pourbabak, J.V. Humbeeck, D. Schryvers: Scr. Mater, 2012, vol.67, no.(12), pp.939–42.
A. Bansiddhi, D.C. Dunand: J. Mater. Eng. Perform, 2011, Vol.20, no. (4), pp.511-516.
A. Bansiddhi, D.C. Dunand: Adv. Eng. Mater., 2011, vol.13, no.(4), pp. 301–05.
M. Piao, S. Miyazaki, K. Otsuka, N. Nishida: Mater. Trans,1992, vol.33, no.(4), pp.337-345.
W.C. Oliver, G.M. Pharr: J. Mater. Res, 1992, vol.7. no.(6), pp.1564-1583.
J.P. Micklich, C. Somsen, A. Dlouhy, C. Begau, A. Hartmaier, M.F. Wagner, G. Eggeler. Acta Mater, 2013, vol.61, no. (2), pp.602-616.
This research was supported by DARPA under the Grant W91CRB1010004. National Science Foundation under Grant No: 51302168 of China. The authors gratefully acknowledge experimental hardness measurements by Dr. Lechun Xie from Shanghai Jiao Tong University.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Manuscript submitted March 13, 2014.
Rights and permissions
About this article
Cite this article
Wang, L., Wang, C. & Dunand, D.C. Microstructure and Strength of NiTi-Nb Eutectic Braze Joining NiTi Wires. Metall Mater Trans A 46, 1433–1436 (2015). https://doi.org/10.1007/s11661-015-2781-z
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-015-2781-z