Nucleation of isolated PO₄ units on CeO₂ driven by high temperatures and the effect on its oxygen storage and release properties

The chemical nature of P-containing species of varying concentration present in CeO₂ after impregnation with (NH₄)₂HPO₄ and calcination at 1273 K, and their effects on the oxygen storage and release (OSR) properties of ceria are reported for the first time. The samples were characterized by different techniques and the results were compared with those recently reported on the same samples but calcined at 873 K. When P-containing ceria solids were calcined at 1273 K, CePO₄ (monazite) was the predominant P-containing species on the surface of ceria, confirming previous studies that showed that monazite exists for those samples in which the surface P loading (P atoms per nm⁻²) is larger than 5.5. For lower surface P concentrations, isolated orthophosphate units are present at the surface and within the subsurface region of the solid. Severe sintering of CeO₂ after calcination at 1273 K resulted in P concentrations >5.5 P atoms·nm⁻² in all samples. Isolated PO₄ units that could initially be present in the samples calcined at 873 K nucleated and CePO₄ was formed when samples were calcined at 1273 K. OSR properties of CeO₂ deteriorated progressively when P loading increased due to the presence of larger crystals of the very stable Ce(III) phase of CePO₄ at the surface of the P-containing ceria solids.