A favorable effect is established for reducing carbon and manganese content in low-alloy pipe steels of strength categories X56–X65 on the increase in hydrogen-induced cracking (HIC) resistance of thick-rolled sheet prepared by a thermomechanical treatment regime. This effect is due to a reduction in segregation structural inhomogeneity in the axial area of sheets in the form of a solid band of high-carbon structures.
Similar content being viewed by others
References
Sour Gas Resistant Pipe Steel. Niobium Information, No. 18/01, CBMM/NPC, Düsseldorf, Germany (2001).
N. Ishikawa, S. Endo, and T. Shinmiya, “High-grade line pipe for heavy sour environment,” 4th Int. Conf. Pipeline Technology, Ostend, Belgium. May 9–13, 2004, pp. 1633–1648.
A. P. Nelyi, O. B. Isaev, Yu. I. Matrosov, and O. A. Nosochenko, Central Segregation Inhomogeneity in Continuously-Cast Sheet Workpieces and Thin Rolled Sheet Metallurgizdat, Moscow (2005).
Yu. I. Matrosov, A. A. Kholodnyi, M. Yu. Matrosov, et al., “Effect of accelerated cooling parameters on microstructure and hydrogen-induced cracking (HIC) resistance of low-alloy pipe steels,” Metallurg, No. 1, 68–75 (2015).
Author information
Authors and Affiliations
Additional information
Translated from Metallurg, No. 1, pp. 54–58, January, 2016.
Rights and permissions
About this article
Cite this article
Kholodnyi, A.A., Matrosov, Y.I., Matrosov, M.Y. et al. Effect of Carbon and Manganese on Low-Carbon Pipe Steel Hydrogen-Induced Cracking Resistance. Metallurgist 60, 54–60 (2016). https://doi.org/10.1007/s11015-016-0251-5
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11015-016-0251-5