Preparation, characterization, and physical properties of graphene nanosheets and films obtained from low-temperature expandable graphite

  • Original Paper
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

Graphene nanosheets have been prepared from low-temperature expandable graphite by ball milling and subsequent ultrasonication. The as-prepared graphene nanosheets were characterized by ultraviolet–visible spectroscopy, Fourier transform infrared spectroscopy, Raman spectroscopy, transmission electron microscopy, atomic force microscopy, differential thermal analysis, etc. The graphene concentration in the suspensions could be increased proportionally by simply extending the milling and ultrasonication duration. The graphene morphology changed from ribbons to single- and few-layer nanosheets with a porous nature. After milling for 40 h, the average number of stacking layers was estimated to be 3.5 for the graphene nanosheets. The lateral dimension of the defect-free crystallites decreased with the milling time, whereas the structural defects mainly from the graphene edges increased accordingly. The exfoliation process was interpreted in terms of complex factors, including weak interlayer attraction, shear-induced dislocation bands, and acoustic cavitation of ultrasonic irradiation. The sheet resistance of the graphene films dramatically decreased after the thermal treatments, especially in reducing atmospheres. This facile approach appears promising for its potential applications in functional composite materials.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  1. Novoselov KS, Geim AK, Morozov SV et al (2004) Electric field effect in atomically thin carbon films. Science 306:666–669

    Article  Google Scholar 

  2. Geim AK (2009) Graphene: status and prospects. Science 324:1530–1534

    Article  Google Scholar 

  3. Jayasena B, Reddy CD, Subbiah S (2013) Separation, folding and shearing of graphene layers during wedge-based mechanical exfoliation. Nanotechnology 24:205301–1–205301–8

    Article  Google Scholar 

  4. Ago H, Ogawa Y, Tsuji M, Mizuno S, Hibino H (2012) Catalytic growth of graphene: toward large-area single-crystalline graphene. J Phys Chem Lett 3:2228–2236

    Article  Google Scholar 

  5. Xue YZ, Wu B, Jiang L et al (2012) Low temperature growth of highly nitrogen-doped single crystal graphene arrays by chemical vapor deposition. J Am Chem Soc 134:11060–11063

    Article  Google Scholar 

  6. Tetlow H, Boer JP, Ford IJ, Vvedensky DD, Coraux J, Kantorovich L (2014) Growth of epitaxial graphene: theory and experiment. Phys Rep 542:195–295

    Article  Google Scholar 

  7. Stankovich S, Dikin DA, Piner RD et al (2007) Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45:1558–1565

    Article  Google Scholar 

  8. Tung VC, Allen MJ, Yang Y, Kaner RB (2009) High-throughput suspension processing of large-scale graphene. Nat Nanotechnol 4:25–29

    Article  Google Scholar 

  9. Gao W, Alemany LB, Ci L, Ajayan PM (2009) New insights into the structure and reduction of graphite oxide. Nat Chem 1:403–408

    Article  Google Scholar 

  10. Knieke C, Berger A, Voigt M, Taylor RNK, Röhr J, Peukert W (2010) Scalable production of graphene sheets by mechanical delamination. Carbon 48:3196–3204

    Article  Google Scholar 

  11. Shang NG, Papakonstantinou P, Sharma S et al (2012) Controllable selective exfoliation of high-quality graphene nanosheets and nanodots by ionic liquid assisted grinding. Chem Commun 48:1877–1879

    Article  Google Scholar 

  12. Coleman JN (2013) Liquid exfoliation of defect-free graphene. Acc Chem Res 46:14–22

    Article  Google Scholar 

  13. Samoilov VM, Danilov EA, Nikolaeva AV et al (2015) Formation of graphene aqueous suspensions using fluorinated surfactant-assisted ultrasonication of pristine graphite. Carbon 84:38–46

    Article  Google Scholar 

  14. Yao YG, Lin ZY, Li Z, Song XJ, Moon KS, Wong CP (2012) Large-scale production of two-dimensional nanosheets. J Mater Chem 22:13494–13499

    Article  Google Scholar 

  15. Paton KR, Varrla E, Backes C et al (2014) Scalable production of large quantities of defect-free few-layer graphene by shear exfoliation in liquids. Nat Mater 13:624–630

    Article  Google Scholar 

  16. Ying ZG, Lin XM, Qia Y, Luo J (2008) Preparation and characterization of low-temperature expandable graphite. Mater Res Bull 43:2677–2686

    Article  Google Scholar 

  17. Jiang BJ, Tian CG, Wang L et al (2010) Facile fabrication of high quality graphene from expandable graphite: simultaneous exfoliation and reduction. Chem Commun 46:4920–4922

    Article  Google Scholar 

  18. Zu CX, Li LJ, Qie L, Manthiram A (2015) Expandable-graphite-derived graphene for next-generation battery chemistries. J Power Sources 284:60–67

    Article  Google Scholar 

  19. Zhang WN, He W, Jing XL (2010) Preparation of a stable graphene dispersion with high concentration by ultrasound. J Phys Chem B 114:10368–10373

    Article  Google Scholar 

  20. Qi XD, Zhou TN, Deng S, Zong GY, Yao XL, Fu Q (2014) Size-specified graphene oxide sheets: ultrasonication assisted preparation and characterization. J Mater Sci 49:1785–1793. doi:10.1007/s10853-013-7866-8

    Article  Google Scholar 

  21. Ai KL, Liu YL, Lu LH, Cheng XL, Huo L (2011) A novel strategy for making soluble reduced graphene oxide sheets cheaply by adopting an endogenous reducing agent. J Mater Chem 21:3365–3370

    Article  Google Scholar 

  22. Li D, Muller MB, Gilje S, Kaner RB, Wallace GG (2008) Processable aqueous dispersions of graphene nanosheets. Nat Nanotechnol 3:101–105

    Article  Google Scholar 

  23. Hernandez Y, Nicolosi V, Lotya M et al (2008) High-yield production of graphene by liquid-phase exfoliation of graphite. Nat Nanotechnol 3:563–568

    Article  Google Scholar 

  24. Hernandez Y, Lotya M, Nicolosi V et al (2009) Liquid phase production of graphene by exfoliation of graphite in surfactant/water suspensions. J Am Chem Soc 131:3611–3820

    Article  Google Scholar 

  25. Park S, Ruoff RS (2009) Chemical methods for the production of graphenes. Nat Nanotechnol 4:217–224

    Article  Google Scholar 

  26. Bao WZ, Miao F, Chen Z et al (2009) Controlled ripple texturing of suspended graphene and ultrathin graphite membranes. Nat Nanotechnol 4:562–566

    Article  Google Scholar 

  27. Geng DS, Yang SL, Zhang Y et al (2011) Nitrogen doping effects on the structure of graphene. Appl Surf Sci 257:9193–9198

    Article  Google Scholar 

  28. Klug HP, Alexander LE (1962) X-ray Diffraction Procedures for Polycrystalline and Amorphous Materials. Wiley, New York

    Google Scholar 

  29. Leng J (2009) Preparation and application of low-temperature expandable graphite with low energy consumption. Master’s thesis, Nanjing University of Technology

  30. Zhang ST, Gu AY, Gao HF, Che XQ (2011) Preparation of exfoliated graphite by intercalating agents of mixed acid. Carbon (in Chinese) 1:3–7

    Google Scholar 

  31. Luong ND, Pahimanolis N, Hippi U et al (2011) Graphene/cellulose nanocomposite paper with high electrical and mechanical performances. J Mater Chem 21:13991–13998

    Article  Google Scholar 

  32. Eda G, Ball J, Mattevi C et al (2011) Partially oxidized graphene as a precursor to graphene. J Mater Chem 21:11217–11223

    Article  Google Scholar 

  33. Sun X, Liu Z, Welsher K et al (2008) Nano-graphene oxide for cellular imaging and drug delivery. Nano Res 1:203–212

    Article  Google Scholar 

  34. Pretsch E, Buhlmann P, Affolter C (2000) Structure Determination of Organic Compounds Table of spectral data. Springer, Berlin Heidelberg

    Book  Google Scholar 

  35. Ju HM, Huh SH, Choi SH, Lee HL (2010) Structures of thermally and chemically reduced graphene. Mater Lett 64:357–360

    Article  Google Scholar 

  36. Acik M, Lee G, Mattevi C, Chhowalla M, Cho K, Chabal YJ (2010) Unusual infrared- absorption mechanism in thermally reduced graphene oxide. Nat Mater 9:840–845

    Article  Google Scholar 

  37. Dey RS, Hajra S, Sahu RK, Raj CR, Panigrahi MK (2012) A rapid room temperature chemical route for the synthesis of graphene: metal-mediated reduction of graphene oxide. Chem Commun 48:1787–1789

    Article  Google Scholar 

  38. Cancado LG, Takai K, Enoki T et al (2006) General equation for the determination of the crystallite size L a of nanographite by Raman spectroscopy. Appl Phys Lett 88:163106–1–163106–3

    Article  Google Scholar 

  39. Cancado LG, Jorio A, Ferreira EHM et al (2011) Quantifying defects in graphene via Raman spectroscopy at different excitation energies. Nano Lett 11:3190–3196

    Article  Google Scholar 

  40. Eckmann A, Felten A, Mishchenko A et al (2012) Probing the nature of defects in graphene by Raman spectroscopy. Nano Lett 12:3925–3930

    Article  Google Scholar 

  41. Ferrari AC, Meyer JC, Scardaci V et al (2006) Raman Spectrum of Graphene and Graphene Layers. Phys Rev Lett 97:18401–1–18401–5

    Google Scholar 

  42. Lv RT, Li Q, Botello-Mendez AR et al (2012) Nitrogen-doped graphene: beyond single substitution and enhanced molecular sensing. Sci Rep 2(586):1–8

    Google Scholar 

  43. Park JS, Reina A, Saito R, Kong J, Dresselhaus G, Dresselhaus MS (2009) G’ band Raman spectra of single, double and triple layer graphene. Carbon 47:1303–1310

    Article  Google Scholar 

  44. Ferreira EHM, Moutinho MVO, Stavale F et al (2010) Evolution of the Raman spectra from single-, few-, and many-layer graphene with increasing disorder. Phys Rev B 82:125429–1–125429–9

    Google Scholar 

  45. Su CY, Xu YP, Zhang WJ et al (2010) Highly efficient restoration of graphitic structure in graphene oxide using alcohol vapors. ACS Nano 4:5285–5292

    Article  Google Scholar 

  46. Wang H, Wang YF, Cao XW, Feng M, Lan GX (2009) Vibrational properties of graphene and graphene layers. J Raman Spectrosc 40:1791–1796

    Article  Google Scholar 

  47. Hasan SA, Tsekoura EK, Sternhagen V, Strømme M (2012) Evolution of the composition and suspension performance of nitrogen-doped graphene. J Phys Chem C 116:6530–6536

    Article  Google Scholar 

  48. Camino G, Duquesne S, Delobel R et al (2001) Fires and Polymers: Materials and Suspensions for Hazard Prevention (Symposium Series No. 797). ACS Pub, Washington, DC

    Google Scholar 

  49. Wang XR, Li XL, Zhang L et al (2009) N-doping of graphene through electrothermal reactions with ammonia. Science 324:758–771

    Article  Google Scholar 

  50. Duan X, Ao Z, Sun H et al (2015) Nitrogen-doped graphene for generation and evolution of reactive radicals by metal-free catalysis. ACS Appl Mater Inter 7:4169–4178

    Article  Google Scholar 

  51. Sandoval S, Kumar N, Sundaresan A, Rao CN, Fuertes A, Tobias G (2014) Enhanced thermal oxidation stability of reduced graphene oxide by nitrogen doping. Chem-Eur J 20:11999–12003

    Article  Google Scholar 

  52. Antisari MV, Montone A, Jovic N, Piscopiello E, Alvania C, Pillonia L (2006) Low energy pure shear milling: a method for the preparation of graphite nanosheets. Scripta Mater 55:1047–1050

    Article  Google Scholar 

  53. Sidorov AN, Bansal T, Jouseph P, Sumanasekera G (2010) Graphene nanoribbons exfoliated from graphite surface dislocation bands by electrostatic force. Nanotechnology 21:195704–1–195704–5

    Article  Google Scholar 

  54. Wang S, Tang LAL, Bao QL et al (2009) Room-temperature synthesis of soluble carbon nanotubes by the sonication of graphene oxide nanosheets. J Am Chem Soc 131:16832–16837

    Article  Google Scholar 

  55. Carotenuto G, Longo A, Nicola SD, Camerlingo C, Nicolais L (2013) A simple mechanical technique to obtain carbon nanoscrolls from graphite nanoplatelets. Nanoscale Res Lett 8(403):1–6

    Google Scholar 

  56. Liu CQ, Hua GX, Gao HY (2012) Preparation of few-layer and single-layer graphene by exfoliation of expandable graphite in supercritical N, N-dimethylformamide. J Supercrit Fluid 63:99–104

    Article  Google Scholar 

  57. Dreyer DR, Murali S, Zhu YW, Ruoff RS, Bielawski CW (2011) Reduction of graphite oxide using alcohols. J Mater Chem 21:3443–3447

    Article  Google Scholar 

  58. Geng JX, Liu LJ, Yang SB et al (2010) A simple approach for preparing transparent conductive graphene films using the controlled chemical reduction of exfoliated graphene oxide in an aqueous suspension. J Phys Chem C 114:14433–14440

    Article  Google Scholar 

  59. Chen CM, Yang YG, Wen YF, Yang QH, Wang MZ (2008) Preparation of ordered graphene-based conductive membrane. New Carbon Mater 23:345–350

    Google Scholar 

  60. Geng JX, Jung HT (2010) Porphyrin functionalized graphene sheets in aqueous suspensions: from the preparation of graphene sheets to highly conductive graphene films. J Phys Chem C 114:8227–8234

    Article  Google Scholar 

  61. Zheng QB, Li ZG, Yang JH, Kim JK (2014) Graphene oxide-based transparent conductive films. Prog Mater Sci 64:200–247

    Article  Google Scholar 

  62. Zhou XF, Liu ZP (2010) A scalable, suspension-phase processing route to graphene oxide and graphene ultralarge sheets. Chem Commun 46:2611–2613

    Article  Google Scholar 

  63. Lee SW, Mattevi C, Chhowalla M, Sankaran RM (2012) Plasma-assisted reduction of graphene oxide at low temperature and atmospheric pressure for flexible conductor applications. J Phys Chem Lett 3:772–777

    Article  Google Scholar 

Download references

Acknowledgements

This work was partially supported by the Natural Science Foundation of China (No.51462024), the Special Project for Fujian Provincial Universities (JK2014055) and the research fund of science and technology of Ningde city (20140218).

Author information

Authors and Affiliations

  1. Department of Physics and Electrical Engineering, Ningde Normal University, Ningde, 352100, China

    Guiqing Guan

  2. School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang, 330063, China

    Jinshan Lu & Hongliu Jiang

Authors
  1. Guiqing Guan
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Jinshan Lu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Hongliu Jiang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Jinshan Lu.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Guan, G., Lu, J. & Jiang, H. Preparation, characterization, and physical properties of graphene nanosheets and films obtained from low-temperature expandable graphite. J Mater Sci 51, 926–936 (2016). https://doi.org/10.1007/s10853-015-9422-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-015-9422-1

Keywords

Search

Navigation