Wood moisture content during the thermal modification process affects the improvement in hygroscopicity of Scots pine sapwood

  • Original
  • Published:
Wood Science and Technology Aims and scope Submit manuscript

Abstract

Elevated wood moisture contents during the thermal modification process have been shown to adversely affect the improvement in dimensional stability and hygroscopicity. This study tested the hypothesis that the effect of elevated wood moisture content is based on the impact of water on chemical reactions which determine the cell wall matrix stiffness. Samples of Scots pine sapwood (Pinus sylvestris L.) were thermally modified in saturated water vapor at different peak temperatures and durations starting either in oven-dry or in water-saturated state. For a given mass loss caused by the modification process, the improvement in maximum swelling and equilibrium moisture content was stronger for oven-dry samples. After removal of water-soluble degradation products, which caused a cell wall bulking effect, the maximum swelling even increased after modification in water-saturated state. Based on dynamic vapor sorption measurements, it was evidenced that the modification in oven-dry state increased the cell wall matrix stiffness which improved dimensional stability and hygroscopicity. Enhanced bond formation in the polymeric network, i.e., via condensation and cross-linking reactions during the treatment of oven-dry wood, is suggested as a cause for this increase in matrix stiffness. In contrast, the modification in water-saturated state enhanced the flexibility of the cell wall matrix, which increased the cell wall swelling and limited the improvement of hygroscopicity to the reduction in OH groups by removal of hemicelluloses. This enhanced matrix flexibility was potentially caused by predominant hydrolytic cleavage of bonds in case of water-saturated samples, evident from the chemical analysis of soluble degradation products, which increased the free volume between adjacent matrix polymers.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4

Similar content being viewed by others

References

  • Altgen M, Willems W, Militz H (2016) Wood degradation affected by process conditions during thermal modification of European beech in a high-pressure reactor system. Eur J Wood Wood Prod. doi:10.1007/s00107-016-1045-y

    Google Scholar 

  • Biziks V, Andersons B, Sansonetti E, Andersone I, Militz H, Grinins J (2015) One-stage thermo-hydro treatment (THT) of hardwoods: an analysis of form stability after five soaking-drying cycles. Holzforschung 69(5):563–571

    Article  CAS  Google Scholar 

  • Borrega M, Kärenlampi P (2008) Effect of relative humidity on thermal degradation of Norway spruce (Picea abies) wood. J Wood Sci 54(4):323–328

    Article  CAS  Google Scholar 

  • Borrega M, Kärenlampi P (2010) Hygroscopicity of heat-treated Norway spruce (Picea abies) wood. Eur J Wood Wood Prod 68(2):233–235

    Article  CAS  Google Scholar 

  • Cermak P, Rautkari L, Horacek P, Saake B, Rademacher P, Sablik P (2015) Analysis of dimensional stability of thermally modified wood affected by re-wetting cycles. BioResources 10(2):3242–3253

    Article  CAS  Google Scholar 

  • Demirbaş A (2000) Mechanisms of liquefaction and pyrolysis reactions of biomass. Energ Convers Manag 41(6):633–646

    Article  Google Scholar 

  • Engelhardt F (1979) Untersuchungen über die Wasserdampfsorption durch Buchenholz im Temperaturbereich von 110 bis 170 °C. Holz Roh Werkst 37(3):99–112

    Article  CAS  Google Scholar 

  • Engelund ET, Thygesen LG, Svensson S, Hill CAS (2013) A critical discussion of the physics of wood–water interactions. Wood Sci Technol 47(1):141–161

    Article  CAS  Google Scholar 

  • Garrote G, Domínguez H, Parajó JC (1999) Hydrothermal processing of lignocellulosic materials. Holz Roh Werkst 57(3):191–202

    Article  CAS  Google Scholar 

  • González-Pena MM, Breese MC, Hale MDC (2005) Studies on the relaxation of heat-treated wood. In: Militz H, Hill C (eds) 2nd European conference on wood modification, Göttingen, Germany, pp 87–90

  • Hill C, Ramsay J, Keating B, Laine K, Rautkari L, Hughes M, Constant B (2012a) The water vapour sorption properties of thermally modified and densified wood. J Mater Sci 47(7):3191–3197

    Article  CAS  Google Scholar 

  • Hill CAS, Keating BA, Jalaludin Z, Mahrdt E (2012b) A rheological description of the water vapour sorption kinetics behaviour of wood invoking a model using a canonical assembly of Kelvin–Voigt elements and a possible link with sorption hysteresis. Holzforschung 66(1):35–47

    Article  CAS  Google Scholar 

  • Himmel S, Mai C (2015) Effects of acetylation and formalization on the dynamic water vapor sorption behavior of wood. Holzforschung 69(5):633–643

    Article  CAS  Google Scholar 

  • Hoffmeyer P, Jensen SK, Jones D, Klinke HB, Felby C (2003) Sorption properties of steam treated wood and plant fibres. In: Van Acker J, Hill C (eds) 1st European conference on wood modification, Ghent, Belgium, pp 177–189

  • Hosseinpourpia R, Adamopoulos S, Mai C (2016) Dynamic vapour sorption of wood and holocellulose modified with thermosetting resins. Wood Sci Technol 50(1):165–178

    Article  CAS  Google Scholar 

  • Ishikawa A, Kuroda N, Kato A (2004) In situ measurement of wood moisture content in high-temperature steam. J Wood Sci 50(1):7–14

    Article  Google Scholar 

  • Kollmann F, Fengel D (1965) Änderungen der chemischen Zusammensetzung von Holz durch thermische Behandlung. Holz Roh Werkst 23(12):461–468

    CAS  Google Scholar 

  • Kotilainen R (2000) Chemical changes in wood during heating at 150–160 °C. Dissertation, University of Jyväskylä, Finland

  • Kubojima Y, Suzuki Y, Tonosaki M, Ishikawa A (2003) Moisture content of green wood in high temperature water vapor. Holzforschung 57(6):634–638

    Article  CAS  Google Scholar 

  • Lenth CA, Kamke FA (2001) Equilibrium moisture content of wood in high-temperature pressurized environments. Wood Fiber Sci 33(1):104–118

    CAS  Google Scholar 

  • Li J, Henriksson G, Gellerstedt G (2007) Lignin depolymerization/repolymerization and its critical role for delignification of aspen wood by steam explosion. Bioresour Technol 98(16):3061–3068

    Article  CAS  PubMed  Google Scholar 

  • Miller GL (1959) Use of dinitrosalicylic acid reagent for determination of reducing sugar. Anal Chem 31(3):426–428

    Article  CAS  Google Scholar 

  • Nuopponen M, Vuorinen T, Jämsä S, Viitaniemi P (2005) Thermal modifications in softwood studied by FT-IR and UV resonance Raman spectroscopies. J Wood Chem Technol 24(1):13–26

    Article  Google Scholar 

  • Popescu C-M, Hill CAS (2013) The water vapour adsorption–desorption behaviour of naturally aged Tilia cordata Mill. wood. Polym Degrad Stabil 98(9):1804–1813

    Article  CAS  Google Scholar 

  • Rautkari L, Hill CAS (2014) Effect of initial moisture content on the anti-swelling efficiency of thermally modified Scots pine sapwood treated in a high-pressure reactor under saturated steam. Holzforschung 68(3):323–326

    Article  CAS  Google Scholar 

  • Rautkari L, Hill CS, Curling S, Jalaludin Z, Ormondroyd G (2013) What is the role of the accessibility of wood hydroxyl groups in controlling moisture content? J Mater Sci 48(18):6352–6356

    Article  CAS  Google Scholar 

  • Runkel RH (1954) Studien über die Sorption der Holzfaser.—Erste Mitteilung: Die Sorption der Holzfaser in morphologische-chemischer Betrachtung. Holz Roh Werkst 12(6):226–232

    Article  CAS  Google Scholar 

  • Runkel RH, Lüthgens M (1956) Untersuchungen über die Heterogenität der Wassersorption der chemischen und morphologischen Komponenten verholzter Zellwände. Holz Roh Werkst 14(11):424–441

    Article  CAS  Google Scholar 

  • Seborg M, Tarkow H, Stamm AJ (1953) Effect of heat upon the dimensional stabilization of wood. J For Prod Res Soc 3(3):59–67

    CAS  Google Scholar 

  • Singleton VL, Rossi JA (1965) Colorimetry of total phenolics with phosphomolybdic–phosphotungstic acid reagents. Am J Enol Vitic 16(3):144–158

    CAS  Google Scholar 

  • Skaar C (1988) Wood–water relations. Springer series in wood science. Springer, Berlin

    Google Scholar 

  • Stamm AJ, Hansen LA (1937) Minimizing wood shrinkage and swelling effect of heating in various gases. Ind Eng Chem 29(7):831–833

    Article  CAS  Google Scholar 

  • Thygesen LG, Engelund ET, Hoffmeyer P (2010) Water sorption in wood and modified wood at high values of relative humidity. Part I: results for untreated, acetylated, and furfurylated Norway spruce. Holzforschung 64(3):315–323

    Article  CAS  Google Scholar 

  • Tjeerdsma BF, Militz H (2005) Chemical changes in hydrothermal treated wood: FTIR analysis of combined hydrothermal and dry heat-treated wood. Holz Roh Werkst 63(2):102–111

    Article  CAS  Google Scholar 

  • Tjeerdsma BF, Boonstra M, Pizzi A, Tekely P, Militz H (1998) Characterisation of thermally modified wood: molecular reasons for wood performance improvement. Holz Roh Werkst 56(3):149–153

    Article  CAS  Google Scholar 

  • Vrentas JS, Vrentas CM (1991) Sorption in glassy polymers. Macromolecules 24(9):2404–2412

    Article  CAS  Google Scholar 

  • Willems W (2014) The water vapor sorption mechanism and its hysteresis in wood: the water/void mixture postulate. Wood Sci Technol 48(3):499–518

    Article  CAS  Google Scholar 

  • Willems W (2015) A critical review of the multilayer sorption models and comparison with the sorption site occupancy (SSO) model for wood moisture sorption isotherm analysis. Holzforschung 69(1):67–75

    CAS  Google Scholar 

  • Willems W, Mai C, Militz H (2013) Thermal wood modification chemistry analysed using van Krevelen’s representation. Int Wood Prod J 4(3):166–171

    Article  Google Scholar 

  • Yasuda R, Minato K, Norimoto M (1994) Chemical modification of wood by non-formaldehyde cross-linking reagents. Wood Sci Technol 28(3):209–218

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Michael Altgen.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Altgen, M., Hofmann, T. & Militz, H. Wood moisture content during the thermal modification process affects the improvement in hygroscopicity of Scots pine sapwood. Wood Sci Technol 50, 1181–1195 (2016). https://doi.org/10.1007/s00226-016-0845-x

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00226-016-0845-x

Keywords

Navigation