Abstract
High-quality, high-Sn-content GeSn/Ge multi-quantum well (MQW) structures were grown on Ge (100) substrates by molecular beam epitaxy. The Sn content of the GeSn layers in the MQWs was 7.85 %. High crystalline quality and smooth interfaces were observed by high-resolution X-ray diffraction (HRXRD) and transmission electron microscopy (TEM). Clear multistage satellite peaks were identifiable in the HRXRD results and were consistent with those obtained in simulations. No threading or misfit dislocations were observed in the TEM images. The room temperature photoluminescence showed an enhanced emission peak of direct transitions around 2025 nm due to the quantum confinement effect. Rapid thermal annealing was also performed and indicated that the MQW structures remained stable when annealed at 400 °C for 30 s. With increasing temperature, the intermixing of the GeSn and Ge layers increased, and the structure completely degenerated at 600 °C. These results will provide a valuable reference for the processing of GeSn devices.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
V.R. D’Costa, C.S. Cook, A.G. Birdwell, C.L. Littler, M. Canonico, S. Zollner, J. Kouvetakis, J. Menedez, Phys. Rev. B 73, 125207 (2006)
C. Guo-En, C. Shu-Wei, C. Shun Lien, IEEE J. Quantum Electron. 46(12), 1813–1820 (2010)
J.Z. Chen, H. Li, H.H. Cheng, G.E. Chang, Opt. Mater. Express 4(6), 1178–1185 (2014)
R. Chen, H. Lin, Y. Huo, C. Hitzman, T.I. Kamins, J.S. Harris, Appl. Phys. Lett. 99(18), 181125 (2011)
A.A. Tonkikh, V.G. Talalaev, P. Werner, Fizikai Tekhnika Poluprovodnikov 47(11), 1462–1466 (2013)
D.L. Zhang, B.W. Cheng, C.L. Xue, X. Zhang, H. Cong, Z. Liu, G.Z. Zhang, Q.M. Wang, Chin. Phys. B 24(2), 024211 (2015)
S. Wirths, R. Geiger, N. von den Driesch, G. Mussler, T. Stoica, S. Mantl, Z. Ikonic, M. Luysberg, S. Chiussi, J.M. Hartmann, H. Sigg, J. Faist, D. Buca, D. Grützmacher, Nat. Photonics 9, 88–92 (2015)
N.J. Ekins-Daukes, K. Kawaguchi, J. Zhang, Cryst. Growth Des. 2(4), 287–292 (2002)
A.A. Tonkikh, C. Eisenschmidt, V.G. Talalaev, N.D. Zakharov, J. Schilling, G. Schmidt, P. Werner, Appl. Phys. Lett. 103(3), 032106 (2013)
G. Sun, R.A. Soref, H.H. Cheng, Opt. Express 18(19), 19957–19965 (2010)
C.D. Thurmond, F.A. Trumbore, M. Kowalchik, J. Chem. Phys. 25(4), 799 (1956)
O. Gurdal, M.-A. Hasan, M.R. Sardela Jr, J.E. Greene, H.H. Radamson, J.E. Sundgren, G.V. Hansson, Appl. Phys. Lett. 67(7), 956–958 (1995)
O. Gurdal, P. Desjardins, J.R. Carlsson, N. Taylor, H.H. Radamson, J.-E. Sundgren, J.E. Greene, J. Appl. Phys. 83(1), 162–170 (1998)
W. Wang, S. Su, J. Zheng, G. Zhang, Y. Zuo, B. Cheng, Q. Wang, Chin. Phys. B 20(6), 068103 (2011)
L. Jiang, C.S. Wu, Y.T. Wang, W.B. Gao, Chin. J. Semicond. 10(2), 86 (1989)
S. Su, D. Zhang, G. Zhang, C. Xue, B. Cheng, Superlattices Microstruct. 64, 543–551 (2013)
X. Zhang, D. Zhang, B. Cheng, Z. Liu, G. Zhang, C. Xue, Q. Wang, ECS Solid State Lett. 3(10), 127–130 (2014)
G.-E. Chang, W.-Y. Hsieh, J.-Z. Chen, H.H. Cheng, Opt. Lett. 38(18), 3485–3487 (2013)
G. Grzybowski, R.T. Beeler, L. Jiang, D.J. Smith, J. Kouvetakis, J. Menendez, Appl. Phys. Lett. 101, 072105 (2012)
Acknowledgments
This work was supported in part by the Major State Basic Research Development Program of China (Grant No. 2013CB632103), the National Natural Science Foundation (Grant Nos. 61435013, 61534005, 61534004, 61377045 and 61411136001) and Beijing Natural Science Foundation (Grant No. 2142031).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhang, X., Liu, Z., He, C. et al. Characterization and thermal stability of GeSn/Ge multi-quantum wells on Ge (100) substrates. J Mater Sci: Mater Electron 27, 9341–9345 (2016). https://doi.org/10.1007/s10854-016-4974-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-4974-7