Abstract
Piezoelectric properties in a Ba(Zr0.075Ti0.925)O3 single crystal were investigated with a consideration that its phase transition lies on room temperatures and the transition can affect piezoelectric properties. The poling treatments were carried with bias fields ranging 2.2 kV/cm∼11 kV/cm at room temperature. The crystal possesses the phase transition from orthorhombic to rhombohedral, lying on room temperature. At 37∘C, the crystal exhibited the excellent piezoelectric properties, a d31 coefficient of over 500 pC/N and a k31 coefficient of 0.38, being caused by the phase transition.
Similar content being viewed by others
References
P.W. Rehrig, S.E. Park, S.T. Mckinstry, G.L. Messing, B. Jones, and T.M. Shrout, J. Appl. Phys., 86, 1657 (1999).
Y. Zhi, R. Guo, and A.S. Bhalla, J. Appl. Phys., 88, 410 (2000).
Z. Yu, C. Ang, R. Guo, and A.S. Bhalla, J. Appl. Phys., 92(3), 1489–1493 (2002).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jeong, SJ., Lee, DS., Park, EC. et al. Piezoelectric properties of a Ba(Zr0.075Ti0.925)O3 single crystal induced by poling treatment. J Electroceram 17, 537–541 (2006). https://doi.org/10.1007/s10832-006-7724-z
Received:
Revised:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10832-006-7724-z