Flow and friction behaviors of 6061 aluminum alloy at elevated temperatures and hot stamping of a B-pillar

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

The flow and friction behaviors of 6061 aluminum alloy (Al6061) at elevated temperatures were investigated to form a B-pillar by hot stamping with Al6061 sheets. The modified Arrhenius and Cowper–Symonds model were developed based on hot tensile tests at temperatures of 350–500 °C and strain rates of 0.01–1 s−1. The coefficients of friction (COF) at temperatures of 300–500 °C were also measured. The tribological test results show that the COF ranged from 0.95 to 1.05 with a loading force of 1 N and from 1.2 to 1.53 with a loading force of 10 N. Finally, hot stamping of a B-pillar using Al6061 sheets with different solution heat treatment temperatures and lubricants was conducted. Stamping experiments show that the B-pillar wrinkled badly and cracked in cold stamping with or without lubricants. The B-pillar also cracked in hot stamping without lubricants, but B-pillars without cracks could be obtained under lubricated conditions. Further finite element simulations with the implementation of Cowper–Symonds constitutive equation and the tested COF values (as references) were used to investigate the crack mechanisms that arise in hot stamping. Simulation results show that the crack was due to adverse friction and large temperature difference between the sidewall and rounded corners caused by non-uniform cooling. Lubrication not only reduces the friction to promote metal flow but also weakens the temperature difference. Thus, parts without cracks can be obtained.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Fakir OE, Wang L, Balint D, Dear JP, Lin J, Dean TA (2014) Numerical study of the solution heat treatment, forming, and in-die quenching (HFQ) process on AA5754. Int J Mach Tools Manuf 87:39–48. https://doi.org/10.1016/j.ijmachtools.2014.07.008

    Article  Google Scholar 

  2. Chen G, Chen M, Wang N, Sun J (2016) Hot forming process with synchronous cooling for AA2024 aluminum alloy and its application. Int J Adv Manuf Technol 86:133–139. https://doi.org/10.1007/s00170-015-8170-3

    Article  Google Scholar 

  3. Garrett RP, Lin J, Dean TA (2005) Solution heat treatment and cold die quenching in forming AA6xxx sheet components: feasibility study. Adv Mater Res 6–8:673–680. https://doi.org/10.4028/www.scientific.net/AMR.6-8.673

    Article  Google Scholar 

  4. Lin J, Dean TA (2005) Modelling of microstructure evolution in hot forming using unified constitutive equations. J Mater Process Technol 167:354–362. https://doi.org/10.1016/j.jmatprotec.2005.06.026

    Article  Google Scholar 

  5. Garrett RP, Lin J, Dean TA (2005) An investigation of the effects of solution heat treatment on mechanical properties for AA 6xxx alloys: experimentation and modelling. Int J Plast 21:1640–1657. https://doi.org/10.1016/j.ijplas.2004.11.002

    Article  MATH  Google Scholar 

  6. Lin J, Mohamed M, Balint D, Dean TA (2013) The development of continuum damage mechanics-based theories for predicting forming limit diagrams for hot stamping applications. Int J Damage Mech 23:684–701. https://doi.org/10.1177/1056789513507731

    Article  Google Scholar 

  7. Xiao W, Wang B, Zheng K (2017) An experimental and numerical investigation on the formability of AA7075 sheet in hot stamping condition. Int J Adv Manuf Technol 92:3299–3309. https://doi.org/10.1007/s00170-017-0419-6

    Article  Google Scholar 

  8. Bai Q, Mohamed M, Shi Z, Lin J, Dean T (2017) Application of a continuum damage mechanics (CDM)-based model for predicting formability of warm formed aluminium alloy. Int J Adv Manuf Technol 88:3437–3446. https://doi.org/10.1007/s00170-016-8853-4

    Article  Google Scholar 

  9. Khamei AA, Dehghani K (2015) Effects of strain rate and temperature on hot tensile deformation of severe plastic deformed 6061 aluminum alloy. Mater Sci Eng A 627:1–9. https://doi.org/10.1016/j.msea.2014.12.081

    Article  Google Scholar 

  10. Zhang C, Yang S, Wang C, Zhao G, Gao A, Wang L (2016) Numerical and experimental investigation on thermo-mechanical behavior during transient extrusion process of high-strength 7×××aluminum alloy profile. Int J Adv Manuf Technol 85:1915–1926. https://doi.org/10.1007/s00170-016-8595-3

    Article  Google Scholar 

  11. Banerjee B, Bhawalkar AS (2008) An extended mechanical threshold stress plasticity model: modeling 6061-T6 aluminum alloy. J Mech Mater Struct 3(3):391–424. https://doi.org/10.2140/jomms.2008.3-3

    Article  Google Scholar 

  12. Ko D, Ko D, Kim J, Park J (2017) Development of a partition panel of an Al6061 sheet metal part for the improvement of formability and mechanical properties by hot forming quenching. Adv Mech Eng 9:1–15. https://doi.org/10.1177/1687814017691213

    Google Scholar 

  13. Ma W, Wang B, Fu L, Zhou J, Huang M (2015) Effect of friction coefficient in deep drawing of AA6111 sheet at elevated temperatures. T Nonferr Metal Soc 25:2342–2351. https://doi.org/10.1016/S1003-6326(15)63849-3

    Article  Google Scholar 

  14. Dohda K, Boher C, Rezai-Aria F, Mahayotsanun N (2015) Tribology in metal forming at elevated temperatures. Friction 3:1–27. https://doi.org/10.1007/s40544-015-0077-3

    Article  Google Scholar 

  15. Wang L, He Y, Zhou J, Duszczyk J (2010) Effect of temperature on the frictional behaviour of an aluminium alloy sliding against steel during ball-on-disc tests. Tribol Int 43:299−306–299−306. https://doi.org/10.1016/j.triboint.2009.06.009

    Google Scholar 

  16. Pellizzari M (2011) High temperature wear and friction behavior of nitrided, PVD-duplex and CVD coated tool steel against 6082 Al alloy. Wear 271:2089–2099. https://doi.org/10.1016/j.wear.2011.01.067

    Article  Google Scholar 

  17. Björk T, Bergström J, Hogmark S (1999) Tribological simulation of aluminium hot extrusion. Wear 224:216−225–216−225. https://doi.org/10.1016/S0043-1648(98)00332-9

    Article  Google Scholar 

  18. Podgornik B, Kosec T, Kocijan A, Donik Č (2015) Tribological behaviour and lubrication performance of hexagonal boron nitride (h-BN) as a replacement for graphite in aluminium forming. Tribol Int 81:267–275. https://doi.org/10.1016/j.triboint.2014.09.011

    Article  Google Scholar 

  19. Gali OA, Riahi AR, Alpas AT (2013) The tribological behavior of AA5083 alloy plastically deformed at warm forming temperatures. Wear 302:1257−1267–1257−1267. https://doi.org/10.1016/j.wear.2012.12.048

    Article  Google Scholar 

  20. Wang L, Zhou J, Duszczyk J, Katgerman L (2012) Identification of a friction model for the bearing channel of hot aluminium extrusion dies by using ball-on-disc tests. Tribol Int 50:66−75–66−75. https://doi.org/10.1016/j.triboint.2012.01.010

    Google Scholar 

  21. Pujante J, Pelcastre L, Vilaseca M, Casellas D, Prakash B (2013) Investigations into wear and galling mechanism of aluminium alloy-tool steel tribopair at different temperatures. Wear 308:193–198. https://doi.org/10.1016/j.wear.2013.06.015

    Article  Google Scholar 

  22. Maeno T, Mori K, Nagai T (2014) Improvement in formability by control of temperature in hot stamping of ultra-high strength steel parts. CIRP Ann Manuf Technol 63:301–304. https://doi.org/10.1016/j.cirp.2014.03.005

    Article  Google Scholar 

  23. Li H, He L, Zhao G, Zhang L (2013) Constitutive relationships of hot stamping boron steel B1500HS based on the modified Arrhenius and Johnson–Cook model. Mater Sci Eng A 580:330–348. https://doi.org/10.1016/j.msea.2013.05.023

    Article  Google Scholar 

  24. Utsunomiya H, Tada K, Matsumoto R (2016) Die motion control for die-quench forging process of AA6061 aluminum alloys. CIRP Ann Manuf Technol 65:297–300. https://doi.org/10.1016/j.cirp.2016.04.132

    Article  Google Scholar 

  25. Keum YT, Ghoo BY (2002) Anisotropy at high temperatures. J Ceram Process Res 3(3):178–181

    Google Scholar 

  26. Coër J, Bernard C, Laurent H, Andrade-Campos A, Thuillier S (2010) The effect of temperature on anisotropy properties of an aluminium alloy. Exp Mech 51:1185–1195. https://doi.org/10.1007/s11340-010-9415-6

    Article  Google Scholar 

  27. Gui Z, Liang W, Liu Y, Zhang Y (2014) Thermo-mechanical behavior of the Al–Si alloy coated hot stamping boron steel. Mater Des 60:26–33. https://doi.org/10.1016/j.matdes.2014.03.011

    Article  Google Scholar 

  28. Cowper G, Symonds P (1957) Strain hardening and strain-rate effects in the impact loading of cantilever beams. Technical Report, Brown University

  29. You L, Hu J, Shi Y, Zhang J (2004) Single-patch surfaces for tool shape design and finite element analysis of hot extrusion. J Mater Process Technol 150:62–69. https://doi.org/10.1016/j.jmatprotec.2004.01.021

    Article  Google Scholar 

  30. Tari DG, Worswick MJ (2015) Elevated temperature constitutive behavior and simulation of warm forming of AZ31B. J Mater Process Technol 221:40–55. https://doi.org/10.1016/j.jmatprotec.2014.12.014

    Article  Google Scholar 

  31. Xu J, Su J, Li Y, Cui J, Sun G, Liu J, Li G (2015) Thermal effects in magnetic pulse forming of magnesium alloy sheet. Int J Adv Manuf Technol 81:755–770. https://doi.org/10.1007/s00170-015-7238-4

    Article  Google Scholar 

  32. Wang K, Jin Y, Zhu B, Zhang Y (2017) Investigation on cracking characteristics of Al–Si coating on hot stamping boron steel parts based on surface strain analysis. Surf Coat Technol 309:282–294. https://doi.org/10.1016/j.surfcoat.2016.11.046

    Article  Google Scholar 

  33. Srinivasulu S, Jain A (2006) A comparative analysis of training methods for artificial neural network rainfall–runoff models. Appl Soft Comput 6:295–306. https://doi.org/10.1016/j.asoc.2005.02.002

    Article  Google Scholar 

  34. Wagener HW, Wolf J (1994) Coefficient of friction in cold extrusion. J Mater Process Technol 44:283–291. https://doi.org/10.1016/0924-0136(94)90441-3

    Article  Google Scholar 

  35. Rech J, Claudin C, D’Eramo E (2009) Identification of a friction model—application to the context of dry cutting of an AISI 1045 annealed steel with a TiN-coated carbide tool. Tribol Int 42:738–744. https://doi.org/10.1016/j.triboint.2008.10.007

    Article  Google Scholar 

  36. Bonnet C, Valiorgue F, Rech J, Claudin C, Hamdi H, Bergheau JM (2008) Identification of a friction model—application to the context of dry cutting of an AISI 316 L austenitic stainless steel with a TiN coated carbide tool. Int J Mach Tools Manuf 48:1211–1223. https://doi.org/10.1016/j.ijmachtools.2008.03.011

    Article  Google Scholar 

  37. Wang L, Zhu B, Wang Q, Zhang Y (2017) Modeling of hot stamping process procedure based on finite state machine (FSM). Int J Adv Manuf Technol 89:857–868. https://doi.org/10.1007/s00170-016-9097-z

    Article  Google Scholar 

  38. Shapiro A (2009) Finite element modeling of hot stamping. Steel Res Int 80:658–664. https://doi.org/10.2374/SRI08SP065

    Google Scholar 

  39. Ji K, Liu X, Fakir OE, Liu J, Zhang Q, Wang L (2016) Determination of the interfacial heat transfer coefficient in the hot stamping of AA7075. Manuf Rev 3:16. https://doi.org/10.1051/mfreview/2016017

    Google Scholar 

  40. Jain VK (1990) Determination of heat transfer coefficient for forging applications. J Mater Shap Technol 8:193–202. https://doi.org/10.1007/BF02833814

    Article  Google Scholar 

  41. Burte PR, Im Y, Altan T, Semiatin SL (1990) Measurement and analysis of heat transfer and friction during hot forging. J Eng Ind 112:332. https://doi.org/10.1115/1.2899596

    Article  Google Scholar 

  42. Zhang X, Zhang L, Xing L (2010) Study of thermal interfacial resistance between TC11/glass lubrication/K403 joint. Exp Thermal Fluid Sci 34:48–52. https://doi.org/10.1016/j.expthermflusci.2009.09.001

    Article  Google Scholar 

  43. Liu X, Ji K, Fakir OE, Fang H, Gharbi MM, Wang L (2017) Determination of the interfacial heat transfer coefficient for a hot aluminium stamping process. J Mater Process Technol 247:158–170. https://doi.org/10.1016/j.jmatprotec.2017.04.005

    Article  Google Scholar 

  44. Borsetto F, Ghiotti A, Bruschi S (2009) Investigation of the high strength steel Al-Si coating during hot stamping operations. Key Eng Mater 410–411:289–296. https://doi.org/10.4028/www.scientific.net/KEM.410-411.289

    Article  Google Scholar 

  45. Riahi M, Nazari H (2011) Analysis of transient temperature and residual thermal stresses in friction stir welding of aluminum alloy 6061-T6 via numerical simulation. Int J Adv Manuf Technol 55:143–152. https://doi.org/10.1007/s00170-010-3038-z

    Article  Google Scholar 

  46. Eiichi O, Yasuhiro Y, Noritoshi I (2015) Deep drawing technique with temperature distribution control for hot stamping process. In: Steinhoff K, Oldenburg M, Prakash B (eds) Proceedings of 5th international conference on hot sheet metal forming of high-performance steel, Toronto, Canada, pp 429–436

  47. Dong Y, Zheng K, Fernandez J, Li X, Dong H, Lin J (2017) Experimental investigations on hot forming of AA6082 using advanced plasma nitrocarburised and CAPVD WC: C coated tools. J Mater Process Technol 240:190–199. https://doi.org/10.1016/j.jmatprotec.2016.09.023

    Article  Google Scholar 

  48. Koroschetz C, Skrikerud M, Jönsson LO (2015) Investigations on aluminium hot forming in comparison to other aluminium forming technologies and the press hardening of steel. In: Steinhoff K, Oldenburg M, Prakash B (eds) Proceedings of 5th international conference on hot sheet metal forming of high-performance steel, Toronto, Canada, pp 437–450

Download references

Acknowledgements

This research work was financially supported by the National Natural Science Foundation of China (Grant No. 51405171), Graduates’ Innovation Fund, Huazhong University of Science and Technology (Grant No. 110-5003110002), and National Natural Science Foundation of China (Grant No. U1564203). The authors would like to acknowledge the Analytic and Testing Center of the Huazhong University of Science and Technology and the State Key Lab of Materials Processing and Die and Mold Technology for their assistance in the SEM characterization, tensile tests, and tribological tests.

Author information

Authors and Affiliations

  1. State Key Laboratory of Materials Processing and Die and Mold Technology, Huazhong University of Science and Technology, Wuhan, Hubei, 430074, China

    Yong Liu, Zhoujie Zhu, Zijian Wang, Bin Zhu, Yilin Wang & Yisheng Zhang

Authors
  1. Yong Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zhoujie Zhu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Zijian Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Bin Zhu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Yilin Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Yisheng Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Bin Zhu.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Liu, Y., Zhu, Z., Wang, Z. et al. Flow and friction behaviors of 6061 aluminum alloy at elevated temperatures and hot stamping of a B-pillar. Int J Adv Manuf Technol 96, 4063–4083 (2018). https://doi.org/10.1007/s00170-018-1790-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-018-1790-7

Keywords

Search

Navigation