Soft magnetic Fe-Co alloys display primary fcc phase solidification for>19,5 at% Co in conventional near-equilibrium solidification processes. Undercooled Fe-Co melt drops within the composition range of 30 to 50 at% Co have been investigated with the electromagnetic levitation technique. The solidification kinetics was measured in situ using a high-resolution Siphotodiode. Melt drops were undercooled up to 263 K below the liquidus temperature and subsequently quenched onto a chill substrate in order to characterize the solidification sequence and microstructure. The transition from stable fcc phase to metastable bcc primary phase solidification has been observed after reaching a critical undercooling level. The critical undercooling increases with rising Co content. The growth velocity drops obviously after transition to metastable bcc phase formation. Parabolic flight experiments were performed in order to study the phase selection under reduced gravity conditions. Under microgravity conditions, a much smaller critical undercooling and an increased life time of the metastable bcc phase were obtained. This result was validated with TEM investigations. The appearance of Fe-O particles gives an indirect hint for an intermediate fcc phase formation from the metastable bcc phase at elevated temperature.
Similar content being viewed by others
References
Savage, S.J., Froes, F.H.: Production of rapidly solidified metals and alloys. JOM, vol. 36, p. 20 (1984).
Herlach, D. M., Cochrane, R. F., Egry, I., Fecht, H.-J., Greer, A. L.: Containerless processing in the study of metallic melts and their solidification. Int. Mat. Rev., vol. 38, p. 273 (1993).
Thoma, D. J., Perepezko, J.H.: Microstructural transitions A during containerless processing of undercooled Fe-Ni alloys. Metall. Trans., vol. 23A, p. 1347 (1992).
Koseki, T., Flemings, M.C.: Solidification of undercooled Fe-Cr-Ni alloys: Part II. Microstructural evolution. Metall. and Mater. Trans. A, vol. 27A, p. 3226 (1996).
Volkmann, T., Löser, W., Herlach, D.M.: Nucleation and phase selection in undercooled Fe-Cr-Ni melts: Part II. Containerless solidification experiments. Metall. and Mater. Trans. A, vol. 28A, p. 461 (1997).
Nishizawa, T. and Ishida, K., in: Binary Alloy Phase Diagrams. Amer. Soc. for Metals, Metals Park OH, Massalski, T.B. (Ed.), p. 1186, (1986).
Sumida, M., Kurz. W.: Peritectic equilibrium in Fe-Co alloys. Z. Metallkde. vol. 93, p. 1154 (2002).
Kim, Y.W., Kelly T.F.: The solidification structures in submicron droplets of Fe-Co alloys. Acta. Metall. Mater. vol. 12, p. 3237 (1991).
Li, M., Lin, X., Song, G., Yang, G., Zhou, Y.: Microstructure evolution and metastable phase formation in undercooled Fe-30 at.% Co melt. Mater. Sci. and Engin. A, vol. 268, p. 90 (1999).
Hermann, R., Löser, W.: Growth kinetics of undercooled Fe-Co melts. J. Magn. Magn. Mat., vol. 242–245, p. 285 (2002).
Löser, W., Garcia-Escorial, A., Vinet, B.: Metastable phase formation in electromagnetic levitation, drop tube and gas-atomization techniques: a comparative study. Int. J. of Non-Equilibrium Processing, vol. 11, 89 (1998).
Matson, D.M., Löser, W., Flemings, M.C., Phase Selection and Rapid Solidification of Undercooled Fe-Cr-Ni Steel Alloys in Microgravity. in: Solidification 1999, Hoffmeister, W.H., Rogers, J.R., Singh, N.B., Marsh, S.P., Vorhees, P.W. (Eds.), TMS, Materials Park OH, p. 99 (1999).
Kurz, W., Fischer, D. J.: Fundamentals of Solidification. Trans Tech Publications, Aedermannsdorf 1992.
Wriedt, H.A. in: Binary Alloy Phase Diagrams, Amer. Soc. for Metals, Metals Park OH, Massalski, T.B. (Ed.), p. 1739 (1986).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hermann, R., Löser, W., Lindenkreuz, H.G. et al. Metastable phase formation in undercooled Fe-Co melts under terrestrial and parabolic flight conditions. Microgravity Sci. Technol 19, 5–10 (2007). https://doi.org/10.1007/BF02870982
Received:
Revised:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02870982