Abstract
The fracture of thick laminated graphite/epoxy composites has been the subject of an extensive research program. The program was divided into three major areas of investigation which included laminate thickness, laminate stacking sequence, and part-through surface flaws. The results from this program are reviewed with emphasis placed on their applicability to the design of thick laminated composite structures.
Similar content being viewed by others
References
Brown, W.F., Jr. and Srawley, J.E., eds., Plane Strain Crack Toughness Testing of High Strength Metallic Materials, ASTM STP 410, Amer. Soc. Test. and Mat. (1966).
Brown, W.F., Jr., ed., Review of Developments in Plane Strain Fracture Toughness Testing, ASTM STP 463, Amer. Soc. Test. and Mat. (1970).
Waddoups, M.E., Eisenmann, J.R. andKaminski, B.E., “Macroscopic Fracture Mechanics of Advanced Composite Materials,”J. Comp. Mat.,5, 446–454 (Oct.1971).
Whitney, J.M. andNuismer, R.J., “Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations,”J. Comp. Mat.,8,253–265 (July1974).
Whitney, J.M. and Nuismer, R.J., “Uniaxial Failure of Composite Laminates Containing Stress Concentrations,” Frac. Mech. of Comp. ASTP STP 593, Amer. Soc. Test. and Mat., 117–142 (1975).
Mandell, J.F., Wang, S.S. and McGarry, F.J., “Fracture of Graphite Fiber Reinforced Composites,” Air Force Mat. Lab. Rep., AFML-TR-73-142 (1973).
Cruse, T.A. and Osias, J.R., “Exploratory Development on Practure Mechanics of Composite Materials,” Air Force Mat. Lab. Rep., AFML-TR-74-111 (1974).
Zweben, C., “An Appoximate Method of Analysis for Notched Unidirectional Composites,”Eng. Frac. Mech.,6 (1),1–10 (1974).
Poe, Jr., C.C., “A Unifying Strain Criterion for Francture of Fibrous Composite Laminates,”Eng. Frac. Mech.,17,153–171 (1983).
Lo, K.H. andWu, E.M., “Serviceability of Composites Surface Damage,”Fibrous Composites in Structural Design, M.E. Lenoe, D.W. Oplinger andJ.J. Burke, eds., Plenum Press, New York (1978).
Sendeckyj, G.P., “Some Observations on Fracture Behavior of Advanced Fiber-Reinforced Laminates,” Proc. 12th Annual Mtg. Soc. Eng. Sci. Univ. of Texas at Austin Press 625–634 (1975).
Wang, S.S. andMandell, J.F., “Analysis of Delamination in Unidirectional and Crossplied Fiber-Composites Containing Surface Cracks,”NASA CR-135248, Nut. Aero. and Space Admin., Washington, D.C. (May1977).
Sendeckyj, G.P., “Surface Notches in Composites,”Fracture of Composite Materials, G.C. Sih andV.P. Tamuzs, eds., Martinus Nijhoff Publishers, Boston, 115–127 (1981).
Sendeckyj, G.P., Maddux, G.E. and Porter, E., “Damage Documentation in Composites by Stereo Radiography,” Damage in Composite Materials, K.L. Reifsnider, ed., ASTM-STP 775, Amer. Soc. Test. and Mat., 16–26 (1982).
Sendeckyj, G.P., “NDE Techniques for Composite Laminates,” AGARD Specialists Mtg. Characterization, Analysis and Significance of Defects in Comp. Mat., London, UK (April 11–14, 1983).
Harris, C.E. andMorris, D.H., “Fracture Behavior of Thick, Laminated Graphite/Epoxy Composites,”NASA CR-3784, Nat. Aero. and Space Admin., Washington, D.C. (1984).
Chu, C.S., Anderson, J.M., Batdorf, W.J. and Aberson, J.A., “Finite Element Computer Program to Analyze Orthotropic Sheets,” NASA CR-2698 (1976).
Harris, C.E. and Morris, D.H., “A Damage Tolerant Design Parameter for Graphite/Epoxy Laminated Composites,”J. Comp. Tech. and Res.,7 (3), (Fall 1985).
Newman, Jr., J.C. and Raju, I.S., “Stress-Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies,” Fracture Mechanics: fourteenth Symposium—Volume I: Theory and Analysis J.C. Lewis and G. Sines, eds., ASTM-STP 791, Amer. Soc. Test. and Mat., I-238-I-265 (1983).
Harris, C.E. and Morris, D.H., “The Fracture of Thick Graphite/ Epoxy Laminates with Part-Through Surface Flaws,” to be published in STP for the ASTM Symp. on Comp. Mat.: Fatigue and Fracture, Dallas, TX, October 1984.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Harris, C., Morris, D. Fracture of thick laminated composites. Experimental Mechanics 26, 34–41 (1986). https://doi.org/10.1007/BF02319953
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02319953