Abstract
The use of an apparatus which is able to fatigue test fibres in a new and original manner has revealed that a fatigue mechanism does exist in nylon fibres. This mechanism is revealed by a distinctive fracture morphology, as seen with the aid of a scanning electron microscope, and failure when the fibre is cycled to loads which, under steady conditions, would not result in fracture. It is shown that a necessary condition for fatigue failure is the cycling of the fibre to a zero minimum load. An explanation for the history and development of such a fatigue break is given.
Similar content being viewed by others
References
J. W. S. Hearle,J. Mater. Sci. 2 (1967) 474.
A. D. M. Nath, Ph.D. thesis (1967) The Victoria University of Manchester.
E. A. Vaughn, Ph.D. Thesis (1969) The Victoria University of Manchester.
J. W. S. Hearle andE. A. Vaughn,Rheologica Acta 9 (1970) 76.
A. R. Bunsell, J. W. S. Hearle, andR. D. Hunter J. Sci. Inst. In press.
J. W. S. Hearle andP. M. Cross,J. Mater. Sci. 5 (1970) 507.
J. W. S. Hearle,Textile Res. J. 36 (1966) 591.
R. Meredith,J. Textile Inst. 45 (1954) T30.
W. T. Kelly,Textile Res. J. 35 (1965) 852.
N. A. Brunt,Kolloid-Z. and Z. für Polymere 239 1, (1970) 561.
C. E. Inglis,Trans. Inst. Naval Archit. 55 (1913) 219.
A. A. Griffith,Phil. Trans. A221 (1921) 163.
R. S. Rivlin andA. J. Thomas,J. Polymer Sci. 10 (1953) 291.
E. H. Andrews, “Fracture in Polymers” (Oliver and Boyd, 1968).
E. H. Andrews, “Testing of Polymers” (Wiley & Sons, edited by W. E. Brown, 1969) p. 237.
D. E. Bosley,Textile Res. J. 38 (1968) 141.
J. W. S. Hearle andB. C. Goswami, Unpublished.
J. Cook andJ. E. Gordon,Proc. Roy. Soc. A282 (1964) 508.
E. H. Andrews,J. Mech. Phys. Solids 11 (1963) 231.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bunsell, A.R., Hearle, J.W.S. A mechanism of fatigue failure in nylon fibres. J Mater Sci 6, 1303–1311 (1971). https://doi.org/10.1007/BF00552044
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00552044