Abstract
Mechanical properties of flax-fibre reinforced composites (FFRC) are strongly affected by water ageing compared to glass-fibre reinforced composites (GFRC). This study highlights the influence of water absorption during immersion at 30 °C on mechanical properties of unsaturated polyester reinforced composites . Flax-fibre composites showed a Fickian absorption behaviour and a water uptake 15 times higher than that of glass-fibre composites. GFRC’s tensile modulus and maximum stress were slightly affected by water uptake while FFRC’s tensile modulus decreased by 37 %, and ultimate stress increased by 34 %. A silane-based chemical treatment (1 % compared to flax fibres) was applied onto flax fibres. Water uptake was slightly reduced by 9 % while tensile modulus at saturation was enhanced by 22 % on treated FFRC compared to untreated ones. Moreover, the complete recovery of the tensile modulus after desiccation suggests that ageing was mainly reversible: fibre and matrix plasticizing phenomena occurred during immersion at 30 °C. No damage was noticed but composites’ initial properties changed with the action of water: further crosslinking of matrix and release of fibre’s small cell-walls components into water were observed. Finally, the drying conditions influenced the return to the initial state before ageing insofar the flax fibres partially lost their initial humidity.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Alix, S., Lebrun, L., Morvan, C., Marais, S., 2011. Study of water behaviour of chemically treated flax fibres-based composites: A way to approach the hydric interface. Compos. Sci. Technol. 71, 893–899.
Assarar, M., Scida, D., Mahi, A. El, Poilâne, C., Ayad, R., 2010. Influence of water ageing on mechanical properties and damage events of two reinforced composite materials: Flax–fibres and glass–fibres. Mater. Des. 32, 788–795.
Azwa, Z.N., Yousif, B.F., Manalo, A.C., Karunasena, W., 2013. A review on the degradability of polymeric composites based on natural fibres. Mater. Des. 47, 424–442.
Baley, C., Perrot, Y., Busnel, F., Guezenoc, H., Davies, P., 2006. Transverse tensile behaviour of unidirectional plies reinforced with flax fibres. Mater. Lett. 60, 2984–2987.
Bergeret, A., Pires, I., Foulc, M.P., Abadie, B., Ferry, L., Crespy, A., 2001. The hygrothermal behaviour of glass-fibre-reinforced thermoplastic composites: a prediction of the composite lifetime. Polym. Test. 20, 753–763.
Bledzki, A.K., Gassan, J., 1999. Composites reinforced with cellulose based fibres. Prog. Polym. Sci. 24, 221–274.
Camino, G., Luda, M.P., Polishchuk, A.Y., Revellino, M., Blancon, R., Merlec, G., 1997. Kinetic aspects of water sorption in polyester-resin/Glass-fibre composites. Compos. Sci. Technol. 51, 1469–1482.
Corn, S., Dupuy, J., Ienny, P., Daridon, L., 2012. Vibration analysis techniques for detecting filler-matrix decohesion in composites. Rev. des Compos. des matériaux avancés 77–90.
Davies, P., Pomiès, F., Carlsson, L., 1996. Influence of Water and Accelerated Aging on the Shear Fracture Properties of Glass/ Epoxy Composite. Appl. Compos. Mater. 3, 71–87.
Dhakal, H., Zhang, Z., Richardson, M., 2007. Effect of water absorption on the mechanical properties of hemp fibre reinforced unsaturated polyester composites. Compos. Sci. Technol. 67, 1674–1683.
Faruk, O., Bledzki, A.K., Fink, H.-P., Sain, M., 2012. Biocomposites reinforced with natural fibers: 2000–2010. Prog. Polym. Sci. 37, 1552–1596.
Fayolle, B., Verdu, J., 2005. Vieillissement physique des matériaux polymères. Tech. L’Ingénieur 1–19.
Fraga, A., Alvarez, V., Vazquez, A., 2003. Relationship between dynamic mechanical properties and water absorption of unsaturated polyester and vinyl ester glass fiber composites. J. Compos. Mater. 37, 1553–1574.
Gautier, L., Mortaigne, B., Bellenger, V., 1999. Interface damage study of hydrothermally aged glass-fibre-reinforced polyester composites. Compos. Sci. Technol. 59, 2329–2337.
Gellert, E.P., Turley, D.M., 1999. Seawater immersion ageing of glass-fibre reinforced polymer laminates for marine applications. Compos. Part A Appl. Sci. Manuf. 30, 1259–1265.
Gibson, R.F., 2000. Modal vibration response measurements for characterization of composite materials and structures. Compos. Sci. Technol. 60, 2769–2780.
Grabovac, I., Turley, D., 1993. Present and future composite materials for marine applications. In: Miravete A, E. (Ed.), Proceedings of the Ninth International Conference on Composite Materials (ICCM-9). Miravete A, editor, Madrid, p. 89.
Joffe, R., Andersons, J., Wallström, L., 2003. Strength and adhesion characteristics of elementary flax fibres with different surface treatments. Compos. Part A Appl. Sci. Manuf. 34, 603–612.
Le Duigou, A., Bourmaud, A., Balnois, E., Davies, P., Baley, C., 2012. Improving the interfacial properties between flax fibres and PLLA by a water fibre treatment and drying cycle. Ind. Crops Prod. 39, 31–39.
Le Duigou, A., Bourmaud, A., Davies, P., Baley, C., 2014. Long term immersion in natural seawater of Flax/PLA biocomposite. Ocean Eng. 90, 140–148.
Le Duigou, A., Davies, P., Baley, C., 2009. Seawater ageing of flax/poly(lactic acid) biocomposites. Polym. Degrad. Stab. 94, 1151–1162.
Mussig, J., 2010. Industrial Applications of Natural Fibres. John Wiley & Sons, Ltd, Chichester, UK.
Pavlidou, S., Papaspyrides, C.., 2003. The effect of hygrothermal history on water sorption and interlaminar shear strength of glass/polyester composites with different interfacial strength. Compos. Part A Appl. Sci. Manuf. 34, 1117–1124.
Pillin, I., Kervoelen, A., Bourmaud, A., Goimard, J., Montrelay, N., Baley, C., 2011. Could oleaginous flax fibers be used as reinforcement for polymers? Ind. Crops Prod. 34, 1556–1563.
Scida, D., Assarar, M., Poilâne, C., Ayad, R., 2013. Influence of hygrothermal ageing on the damage mechanisms of flax-fibre reinforced epoxy composite. Compos. Part B Eng. 48, 51–58.
Shah, D.U., 2014. Natural fibre composites: Comprehensive Ashby-type materials selection charts. Mater. Des. 62, 21–31.
Smith, C.S., 1990. Design of marine structures in composite materials. Elsevier Science Publishers, London.
Xie, Y., Hill, C. a. S., Xiao, Z., Militz, H., Mai, C., 2010. Silane coupling agents used for natural fiber/polymer composites: A review. Compos. Part A Appl. Sci. Manuf. 41, 806–819.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2016 RILEM
About this paper
Cite this paper
Apolinario, G., Ienny, P., Corn, S., Léger, R., Bergeret, A., Haudin, JM. (2016). Effects of Water Ageing on the Mechanical Properties of Flax and Glass Fibre Composites: Degradation and Reversibility. In: Fangueiro, R., Rana, S. (eds) Natural Fibres: Advances in Science and Technology Towards Industrial Applications. RILEM Bookseries, vol 12. Springer, Dordrecht. https://doi.org/10.1007/978-94-017-7515-1_14
Download citation
DOI: https://doi.org/10.1007/978-94-017-7515-1_14
Published:
Publisher Name: Springer, Dordrecht
Print ISBN: 978-94-017-7513-7
Online ISBN: 978-94-017-7515-1
eBook Packages: EngineeringEngineering (R0)